A sonochemical method for direct preparation of nanowires of SbS(1-x)Se(x)I solid solution has been established. The SbS(1-x)Se(x)I gel was synthesized using elemental Sb, S, Se and I in the presence of ethanol under ultrasonic irradiation (35kHz, 2W/cm(2)) at 50 degrees C for 2h. The product was characterized by using techniques such as powder X-ray diffraction, scanning electron microscopy, high-resolution transmission electron microscopy, energy dispersive X-ray analysis, selected area electron diffraction, and optical diffuse reflection spectroscopy. The SEM and HRTEM investigations exhibit that the as-prepared samples are made up of large quantity nanowires with lateral dimensions of about 10-50nm and lengths reaching up to several micrometers and single-crystalline in nature. The increase of molar composition of Se affects linear decrease of the indirect forbidden optical energy gap as well as the distance between (121) planes of the SbS(1-x)Se(x)I nanowires.
RESUMO
The substantiated isolation of the antimony subiodide (Sb(3)I) is presented for the first time. It has been prepared using elemental Sb and I in ethanol under ultrasonic irradiation at 323 K. Its composition was characterized using X-ray photoelectron spectroscopy (XPS) and energy dispersive X-ray analysis (EDAX). The scanning electron microscopy (SEM) and high-resolution transmission electron microscopy (HRTEM) investigations exhibit that the samples are made up of large quantity of nanoparticles with diameters smaller than 20 nm and single crystalline in nature. The interplanar spacings in Sb(3)I that have been determined using powder X-ray diffraction (XRD), selected area electron diffraction (SAED) and HRTEM are very similar. Surprisingly, the registered XRD patterns are identical to the one reported earlier for Sb(4)O(5)I(2).