RESUMO
The objective of this study is to elucidate the influence of a loading procedure of iridium and copper oxides over cordierite honeycomb support on catalytic performance during the decomposition of a hydroxylammonium nitrate (HAN) solution. Iridium and copper composite oxides were successfully supported on the cordierite honeycomb at the same time by repeating the wash coating process more than 2 times. Through the wash coating process, Cu and Ir were supported up to 43.4% and 4.9%, respectively. The cordierite honeycomb without active metal plays little role as a catalyst to lower the decomposition temperature. It was found that IrCu/honeycomb-2 catalyst, which was prepared by repeating the wash coating procedure twice, is an optimal catalyst for the decomposition of HAN solution. The IrCu/honeycomb-2 catalyst had the effect of lowering the decomposition onset temperature by 27.1°C compared to thermal decomposition.
RESUMO
The catalytic decomposition of hydroxylammonium nitrate (HAN) was investigated using a series of platinum and iridium supported on mesoporous materials. In this study, MMZY, KIT-6, and SBA-15 were used as supports. The effects of the active metal and the pore structure of the catalysts on decomposition of HAN solution were studied. The activity of the platinum catalysts supported on mesoporous material is much superior to that of the iridium catalysts on the same support. The Pt(10)/SBA-15 catalyst showed excellent decomposition activity and was the best among the catalysts tested here, which seemed to be because of the pore structure of Pt(10)/SBA-15. Because the pore size of Pt(10)/SBA-15 is larger than that of Pt(10)/MMZY and Pt(10)/KIT-6, it is more advantageous for diffusion of reactant and product gas. The activity of the catalyst increased as the amount of Pt loaded on the SBA-15 support increased.