Hall Effect in Bulk-Doped Organic Single Crystals.

The standard technique to separately and simultaneously determine the carrier concentration per unit volume (N, cm-3 ) and the mobility (µ) of doped inorganic single crystals is to measure the Hall effect. However, this technique has not been reported for bulk-doped organic single crystals. Here, the Hall effect in bulk-doped single-crystal organic semiconductors is measured. A key feature of this work is the ultraslow co-deposition technique, which reaches as low as 10-9 nm s-1 and enables us to dope homoepitaxial organic single crystals with acceptors at extremely low concentrations of 1 ppm. Both the hole concentration per unit volume (N, cm-3 ) and the Hall mobility (µH ) of bulk-doped rubrene single crystals, which have a band-like nature, are systematically observed. It is found that these rubrene single crystals have (i) a high ionization rate and (ii) scattering effects because of lattice disturbances, which are peculiar to this organic single crystal.

FET performance and substitution effect on 2,6-dithienylanthracene devices prepared by photoirradiation of their diketone precursors.

Hole mobility was evaluated by top-contact bottom gate field effect transistor and time resolved microwave conductivity measurements in 2,6-dithienylanthracene and hexyl-substituted 2,6-dithienylanthracene films prepared by spin-coating of their α-diketone precursors followed by photoirradiation, revealing enough high potentials for semiconducting films with charge carrier mobilities of 0.8-0.9 cm(2) V(-1) s(-1) in the photo-irradiated films.