Comparison of conventional impression making and intraoral scanning for the study of unilateral cleft lip and palate.

Patients with cleft lip and palate (CLP) encounter various problems, including disorders related to feeding, esthetics, and pronunciation. We compared two impression methods, conventional impression making and intraoral scanning, to study unilateral cleft lip and palate (UCLP). Patients with UCLP (n = 7) were selected, and palatal impressions were taken by two steps: (1) impressions were obtained using an addition silicone rubber impression material, and a plaster model was prepared and (2) optical impressions were obtained using a desktop three-dimensional (3D) scanner and stereolithography (STL). Data were generated by two impression system combinations through STL. The results were analyzed using the Kruskal-Wallis or Mann-Whitney U test. There were no significant differences in the dimensions of the models between both groups. The measured depth of the alveolar cleft defects was deeper in the plaster model group (STL) than in the intraoral scanner group (STL). Digital models may prevent the risk of aspiration and respiratory disorders by using impression materials for preoperative jaw treatment of newborns and infants. We compared the results of both impression methods in the same patient and found that a shift to the 3D printer model is a safe alternative for preoperative jaw correction, as evidenced from the amount of tissue displaced due to the pressure applied during impression taking. In the future, we would like to conduct clinical research with a larger sample size of CLP patients to further corroborate these findings.

Bonding of Fused Quartz with an Aromatic Silane Compound and Acidic Functional Monomers with a Tri-n-butylborane Initiated Resin.

Purpose: This study evaluated the effect of an aromatic silane compound and acidic functional monomer on the bond strength of fused quartz. Materials and Methods: A total of 264 disk specimens were fabricated from fused quartz for shear bond testing. Two silane compounds were used: 3-(trimethoxysilyl)propyl methacrylate (3-TMSPMA) and 3-(4-methacryloyloxyphenyl) propyltrimethoxysilane (3-MPPTS). As acidic functional monomers, 4-methacryloyloxyethyl trimellitate (4-MET) and 10-methacryloyloxydecyl dihydrogen phosphate (10-MDP) were used. The disks were primed with one of each silane compound with or without the acidic functional monomer of the same molarity. The specimens were bonded with a tri-n-butylborane (TBB) initiated luting material. The shear bond strength was determined before and after 10,000 thermocycles. Bond strength was statistically evaluated with Kruskal-Wallis, Mann-Whitney U-, and Steel- Dwass tests. To test dye penetration, the specimens were immersed in 0.5 wt% fuchsin solution for 24 h after priming with each condition, bonding, and 10,000 thermocycles. The dye penetration area was determined by observing the backside of the bonded specimen with an optical microscope. The relationship between the shear bond strength and dye penetration ratio was analyzed with Spearman's rank correlation test. Results: The highest post-thermocycling bond strengths in the 1 mol% and 2 mol% groups were 3-TMSPMA + 10- MDP and 3-MPPTS + 10-MDP. Spearman's rank correlation coefficient between shear bond strength and dye penetration area was γ = -0.7519, indicating a strong negative correlation. Conclusion: The surface treatments of 3-TMSPMA and 3-MPPTS combined with 10-MDP yielded higher bond strength after 10,000 thermocycles than those combined with 4-MET, despite the similarity in molarity. The shear bond strength was negatively correlated with the dye penetration area.

Castability and mechanical properties of Ti-15Mo-5Zr-3Al alloy in dental casting.

The castability, mechanical properties, and fracture characteristics of Ti-15Mo-5Zr-3Al alloy were compared with those of Ti-6Al-7Nb alloy and pure titanium (CP Ti) for application of this ß-type titanium alloy in cast dental prostheses. Cast specimens were prepared with a centrifugal casting machine. A tensile test was performed according to ISO standard 22674. The castability index for Ti-15Mo-5Zr-3Al was lower than those for Ti-6Al-7Nb and CP Ti. The tensile strength of Ti-15Mo-5Zr-3Al was 852 MPa, which was lower than that of Ti-6Al-7Nb and higher than that of CP Ti. The proof strength of Ti-15Mo-5Zr-3Al was 799 MPa, which was comparable to that of Ti-6Al-7Nb and higher than that of CP Ti. The elastic modulus of Ti-15Mo-5Zr-3Al was 81.0 GPa, which was lower than the values for Ti-6Al-7Nb and CP Ti. Elongation of Ti-15Mo-5Zr-3Al was 5.1%, which was comparable to that of Ti-6Al-7Nb and less than that of CP Ti. The shape of the fractured segment was narrower for Ti-15Mo-5Zr-3Al than for Ti-6Al-7Nb and CP Ti. The deformation characteristics of Ti-15Mo-5Zr-3Al may result in decreased stress relative to increased strain during plastic deformation in the stress-strain diagram. In conclusion, Ti-15Mo-5Zr-3Al alloy has a low elastic modulus and exhibits limited ductile plastic deformation in cast dental prostheses.

Effect of silane compounds on bonding to fused quartz of tri-n-butylborane initiated resin.

This study aimed to investigate how different compositions of experimental silane-based primers in a methyl methacrylate solution containing 3-(trimethoxysilyl)propyl methacrylate (3-TMSPMA) or 3-(4-methacryloyloxyphenyl)propyl trimethoxysilane (3-MPPTS) might act as silicon dioxide bonding agents. With or without post-silanization heat treatment, primer-treated quartz discs were bonded using the MMA-TBB resin and their bond strengths were evaluated. The disks were primed with one of the following materials: 1 mol% 3-TMSPMA, 2 mol% 3-TMSPMA, 1 mol% 3-MPPTS, and 2 mol% 3-MPPTS. Shear bond strength was determined both before and after thermocycling. Statistical analyses were performed with non-parametric procedure (Kruskal-Wallis, Mann-Whitney U, and Steel-Dwass tests). Both primers were effective with heat treatment to enhance bonding between quartz and the MMA-TBB, and the bonding durability of the 1 and 2 mol% 3-MPPTS (16.8 and 24.9 MPa) with heat groups was significantly higher than in the 1 and 2 mol% 3-TMSPMA (5.4 and 9.8 MPa) with heat groups.

Surface roughness and gloss of current CAD/CAM resin composites before and after toothbrush abrasion.

The purpose of this study was to evaluate the gloss and surface roughness behaviors of newly developed CAD/CAM composite blocks with different filler contents and characteristics. The gloss and surface roughness were quantified before and after a toothbrush dentifrice abrasion test; the results were compared to the gloss and surface roughness of a ceramic CAD/CAM block. Knoop hardness was determined before abrasion test. The results were analyzed by ANOVA, Tukey HSD, and Dunnett t test (p<0.05). The rank order of Knoop hardness was as follows: Vita Mark II>Vita Enamic>Gradia block>Shofu Block HC, Lava Ultimate≥Katana Avencia block≥Cerasmart. After toothbrush abrasion, a significant difference in the gloss unit was detected between the Shofu Block HC material and the ceramic block. The Ra and Rz of the Cerasmart and Shofu Block HC materials were significantly larger than those of the ceramic block after toothbrush abrasion.