Optimization of heat treatment parameters of medium carbon steel quenched in different media using Taguchi method and grey relational analysis.

Quenching is one of the major processes of heat treatment of medium carbon steel that aims at improving its mechanical properties. However, the effectiveness of this process is dependent on several control factors that must be maximized to obtain optimum results in terms of hardness, yield strength, ultimate tensile strength among others. This study aims at optimizing the process of improving the mechanical properties of medium carbon steel by varying some key factors like the quenchant used (A), heat treatment temperature (B), and soaking time (C). The measured responses in this study were the hardness, yield strength (YS), and ultimate tensile strength (UTS). Optimization was conducted in two stages. The first stage dealt with the mono-optimization of process parameters using Taguchi's Signal-to-Noise (S/N) ratio. A total of nine (9) experiments were performed based on standard L9 orthogonal array because each of the three control factors has three (3) levels. The second stage was multi-objective optimization using Taguchi-based grey relational analysis (GRA). The optimal conditions for hardness, YS, and UTS were obtained at A2B3C3, A3B2C3, and A3B3C3, respectively. Using ANOVA as statistical analysis, it was observed that the soaking time was the main control factor for all three measured responses (31.95% contribution ratio for hardness, 62.46%, and 66.76% for YS and UTS, respectively), while the quenchant had the least contribution. Analysis of the Taguchi-based GRA revealed that the results obtained are in total conformance to that of the Taguchi method, with soaking time having the highest contribution ratio of 69.41%.

Experimental data on mechanical properties evaluation of medium carbon steel quenched in different waste media.

Several wastes can be instrumental in the improvement of the mechanical properties of medium carbon steel when quenched. The quenching media employed such as coconut water (CW), pap water (PW) and spent engine oil (SPE) have been largely considered as wastes. The data in this article are related to the research article titled "Mechanical Properties Improvement Evaluation of Medium Carbon Steels Quenched in Different Media" (Ikubanni et al., 2017) [1]. The article provides information on the mechanical properties evaluation of medium carbon steel quenched in different media. Twenty-seven (27) samples of medium carbon steel samples were heated to temperatures of 730 °C, 760 °C and 790 °C and soaked for 30, 45 and 60 min respectively. The test results recorded include hardness value, yield strength (YS) and the ultimate tensile strength (UTS) for each of the samples at different heating temperatures and soaking time for the different quenching media.