RESUMO
Transport and thermodynamic properties of a sintered pellet of the newly discovered MgB2 superconductor have been measured to determine the characteristic critical magnetic fields and critical current densities. Both resistive transition and magnetization data give similar values of the upper critical field, Hc2, with magnetization data giving dHc2/dT = 0.44 T/K at the transition temperature of Tc = 40.2 K. Close to the transition temperature, magnetization curves are thermodynamically reversible, but at low temperatures the trapped flux can be on the order of 1 T. The value of dHc/dT at Tc is estimated to be about 12 mT/K, a value similar to classical superconductors like Sn. Hence, the Ginzburg-Landau parameter kappa approximately 26. Estimates of the critical supercurrent density, Jc, using hysteresis loops and the Bean model, give critical current densities on the order of 10(5) A/cm2. Hence the supercurrent coupling through the grain boundaries is comparable to intermetallics like Nb3Sn.
RESUMO
MgB2 becomes superconducting just below 40 K. Whereas porous polycrystalline samples of MgB2 can be synthesized from boron powders, in this Letter we demonstrate that dense wires of MgB2 can be prepared by exposing boron filaments to Mg vapor. The resulting wires have a diameter of 160 microm, are better than 80% dense, and manifest the full chi = -1/4pi shielding in the superconducting state. Temperature-dependent resistivity measurements indicate that MgB2 is a highly conducting metal in the normal state with rho(40 K) = 0.38 microOmega cm. By using this value, an electronic mean-free path, l approximately 600 A can be estimated, indicating that MgB2 wires are well within the clean limit. Tc, Hc2(T), and Jc data indicate that MgB2 manifests comparable or better superconducting properties in dense wire form than it manifests as a sintered pellet.
RESUMO
Two polytypes of potassium rare-earth-metal hexaselenodiphosphates(IV), K(RE)P(2)Se(6) (RE = Y, La, Ce, Pr, Gd), have been synthesized from the stoichiometric reaction of RE, P, Se, and K(2)Se(4) at 750 degrees C. Both single-crystal and powder X-ray diffraction analyses showed that the structures of these polytypes vary with the size of the rare earth metals. For the smaller rare-earth metals, Y and Gd, K(RE)P(2)Se(6) crystallized in the orthorhombic space group P2(1)2(1)2(1). The yttrium compound was studied by single-crystal X-ray diffraction with the cell parameters a = 6.7366(5) Å, b = 7.4286(6) Å, c = 21.603(2) Å, and Z = 4. This structure type comprises a layered, square network of yttrium atoms that are bound to four distinct [P(2)Se(6)](4)(-) units through selenium bonding. Each [P(2)Se(6)](4)(-) unit possesses a Se atom that is not bound to any Y atom but is pointing out into the interlayer spacing, into an environment of potassium cations. For larger rare-earth metals, La, Ce, and Pr, K(RE)P(2)Se(6) crystallized in a second, monoclinic polytype, the structure of which has been published. Both of these two different polytypes can be related to each other and several other isoelectronic chalcophosphate structures based on a Parthé valence electron concentration analysis. These structures include Ag(4)P(2)S(6), K(2)FeP(2)S(6), and the hexagonal M(II)PS(3) structure types. The magnetic susceptibilities of the title compounds have been studied, and the behavior can been explained based on a simple set of unpaired f-electrons. The diffuse reflectance spectroscopy also showed that these yellow plates are moderately wide band gap ( approximately 2.75 eV) semiconductors.