RESUMO
The aim of this study was to compare surface roughness and gloss of resin composites polished using different polishing systems. Five resin composites were investigated: Filtek Silorane (FS), IPS Empress Direct (IP), Clearfil Majesty Posterior (CM), Premise (PM), and Estelite Sigma (ES). Twenty-five disk specimens were prepared from each material, divided into five groups, each polished with one of the following methods: Opti1Step (OS), OptiDisc (OD), Kenda CGI (KD), Pogo (PG), or metallurgical polishing (ML). Gloss and roughness parameters (Sa, Sz, Sq, and St) were evaluated by 60°-angle glossimetry and white-light interferometric profilometry. Two-way analysis of variance was used to detect differences in different materials and polishing techniques. Regression and correlation analyses were performed to examine correlations between roughness and gloss. Significant differences in roughness parameters and gloss were found according to the material, type of polishing, and material/polishing technique (p< 0.05). The highest roughness was recorded when KD was used (Sa: 581.8 [62.1] for FS/KD, Sq: 748.7 [55.6] for FS/KD, Sz: 17.7 [2.7] for CM/KD, and St: 24.6 [6.8] for FS/KD), while the lowest was recorded after ML (Sa: 133.6 [68.9] for PM/ML, Sq: 256.5 [53.5] for ES/ML, Sz: 4.0 [1.3] for ES/ML, and St: 7.1 [0.7] for ES/ML). The highest gloss was recorded for PM/ML (88.4 [2.3]) and lowest for FS/KD (30.3 [5.7]). All roughness parameters were significantly correlated with gloss (r= 0.871, 0.846, 0.713, and 0.707 for Sa, Sq, Sz, St, and gloss, respectively). It was concluded that the polishing procedure and the type of composite can have significant impacts on surface roughness and gloss of resin composites.