Advanced Bioresin Formulation for 3D-Printed Bone Scaffolds: PCLDMA and p-PLA Integration.

In bone tissue engineering, scaffold attributes such as pore dimensions and mechanical strength are crucial. This study synthesized polycaprolactone dimethacrylate (PCLDMA) from polycaprolactone (PCL), incorporating epichlorohydrin (Epi-PCL) and methacryloyl chloride (Meth-Cl). PCLDMA was blended with polylactic acid (p-PLA) to 3D-print bone scaffolds using stereolithography (SLA). Analytical techniques included nuclear magnetic resonance (NMR), Fourier-transform infrared spectroscopy (FTIR), scanning electron microscopy (SEM), and compression testing. Degradation kinetics and cell viability were investigated using human osteoblast (HOB) cells. Findings revealed PCLDMA/p-PLA composite scaffold superiority over the original polymers. Notably, PCLDMA-60 (60% PCLDMA, 40% p-PLA) displayed optimal properties. Compressive strength varied from 0.019 to 16.185 MPa, porosity from 2% to 50%, and degradation rates from 0% to 0.4% over three days. Cell viability assays affirmed biocompatibility across various PCLDMA ratios. In conclusion, PCLDMA/p-PLA composite scaffolds, particularly PCLDMA-60, show great potential in bone tissue engineering.

Plasmon-Sensitized Silica-Titanium Aerogels as Potential Photocatalysts for Organic Pollutants and Bacterial Strains.

Photocatalysis reactions are of great interest as an effective tool against the profusely increasing population of antibiotic-resistant bacteria species. In particular, the promising evidence on plasmon-sensitized titanium dioxide (TiO2) photocatalysis inspired us to investigate their antibacterial activity stemming from the photogenerated reactive oxygen species (ROS). Herein, TiO2 nanostructures were grown in situ within a silica (SiO2) aerogel matrix with high surface area and porosity, and their ROS-related phototoxic effects against Escherichia coli bacteria were investigated under solar- and visible-light irradiations. Photodegradation profiles obtained from Rhodamine B (RhB) organic dye used as a chemical probe proved that the types of ROS produced by SiO2/TiO2 aerogels varied depending on the electromagnetic spectrum portion that was used during material irradiation. Further, the SiO2/TiO2 aerogel matrix was decorated with silver-gold nanostars (Ag@Au NSs) to enhance its photocatalytic efficiency under visible light irradiations. Our design showed that plasmon-enriched composite aerogels efficiently boosted ROS production under visible light exposures and that the structures containing Ag@Au NSs showed a much more effective antibacterial effect compared to their counterparts.

The Biocompatibility of a New Type of 45S5 Bioactive Graft in a Sheep Model: A Pilot Study.

Background Bone is a dramatically regenerating tissue with the ability to heal after trauma, although intensive surgical management is required to treat considerable damage. In this study, 45S5 bioactive grafts were prepared through the melt-quenched method in compliance with the guidelines on medical product requirements (MDD regulations; 93/42/EEC Annex-II section 3&4 and ISO standardizations; ISO 13485:2016) for bone repair and regeneration. Methodology After preparing the graft/scaffold, it was evaluated for biocompatibility according to the principles of "lSO 10993-6 2015 Biological evaluation of medical devices: Tests for local effects after implantation, Annex D 'Test method for implantation in bone,'" "lSO 10993-2:2005 Biological evaluation of medical devices: Animal welfare requirements," and "lSO 10993-12 2012 Biological evaluation of medical devices sample preparation rules and standards." Defects were created on the tibia of the right hind leg. The defects were filled with 3-mm bioactive granules, and a cylindrical polypropylene biocompatible material was used as a negative control. After 120 days, the sheep were sacrificed, and the tibia were analyzed. Results The results demonstrated the safety of 45S5 bioactive grafts. Histological evaluation showed no signs of pathological changes around the implant area. Hematoxylin and eosin sections demonstrated the presence of a few multinucleated giant cells, macrophages, and non-irritant mild fibrotic changes on the surface of the biomaterial. Conclusions 45S5 bioactive glass was found to be biocompatible in a sheep model, demonstrating its capacity to promote bone consolidation while also justifying its further preclinical application as a bone-bonded material owing to the layer formation of the growing bone mineral.

Evaluation of biocomposite putty with strontium and zinc co-doped 45S5 bioactive glass and sodium hyaluronate.

The application of powder or granule formed bioactive glasses in the defect area with the help of a liquid carrier to fill the defects is a subject of interest and is still open to development. In this study, it was aimed to prepare biocomposites of bioactive glasses incorporating different co-dopants with a carrier biopolymer and to create a fluidic material (Sr and Zn co-doped 45S5 bioactive glassessodium hyaluronate). All biocomposite samples were pseudoplastic fluid type, which may be suitable for defect filling and had excellent bioactivity behaviors confirmed by FTIR, SEM-EDS and XRD. Biocomposites with Sr and Zn co-doped bioactive glass had higher bioactivity considering the crystallinity of hydroxyapatite formations compared to biocomposite with undoped bioactive glasses. Biocomposites with high bioactive glass content had hydroxyapatite formations with higher crystallinity compared to biocomposites with low bioactive glass. Furthermore, all biocomposite samples showed non-cytotoxic effect on the L929 cells up to a certain concentration. However, biocomposites with undoped bioactive glass showed cytotoxic effects at lower concentrations compared to biocomposites with co-doped bioactive glass. Thus, biocomposite putties utilizing Sr and Zn co-doped bioactive glasses may be advantageous for orthopedic applications due to their specified rheological, bioactivity, and biocompatibility properties.

Fabrication and characterization of strontium incorporated 3-D bioactive glass scaffolds for bone tissue from biosilica.

Bioactive glass scaffolds that contain silica are high viable biomaterials as bone supporters for bone tissue engineering due to their bioactive behaviour in simulated body fluid (SBF). In the human body, these materials help inorganic bone structure formation due to a combination of the particular ratio of elements such as silicon (Si), calcium (Ca), sodium (Na) and phosphorus (P), and the doping of strontium (Sr) into the scaffold structure increases their bioactive behaviour. In this study, bioactive glass scaffolds were produced by using rice hull ash (RHA) silica and commercial silica based bioactive glasses. The structural properties of scaffolds such as pore size, porosity and also the bioactive behaviour were investigated. The results showed that undoped and Sr-doped RHA silica-based bioactive glass scaffolds have better bioactivity than that of commercial silica based bioactive glass scaffolds. Moreover, undoped and Sr-doped RHA silica-based bioactive glass scaffolds will be able to be used instead of undoped and Sr-doped commercial silica based bioactive glass scaffolds for bone regeneration applications. Scaffolds that are produced from undoped or Sr-doped RHA silica have high potential to form new bone for bone defects in tissue engineering.