Low-Temperature Synthesis of Bi2S3 Hierarchical Microstructures via Co-Precipitation and Digestive Process in Aqueous Medium.

Bismuth sulfide (Bi2S3) nanostructures have gained significant attention in the fields of catalysis, optoelectronics, and biomedicine due to their unique physicochemical properties. This paper introduces a simple and cost-effective method for producing Bi2S3 microstructures at low temperatures (25 and 70 °C). These microstructures are formed by the hierarchical self-assembly of Bi2S3 nanoparticles, which are typically 15-40 nm in size. The nanoparticles are synthesized by the co-precipitation of thioglycolic acid, thioacetamide, and bismuth nitrate in water. The study delves into the phase composition and morphological evolution of the microstructures, concerning the chemical composition of the solution and the synthesis temperature. X-ray analysis has confirmed the formation of single-phase bismuthinite Bi2S3. The synthesis process generates primary building blocks in the form of 15-40 nm Bi2S3 nanocrystals, which then go through a hierarchical self-assembly process to produce a range of micrometer-sized structures. A scanning electron microscopy examination revealed that the primary nanoparticles self-assemble into quasi-1D worm-like nanostructures, which then self-assemble to create sponge-shaped microstructures. These structures subsequently self-organize and refine into either flower- or dandelion-like microstructures, mostly depending on the synthesis temperature and the chemistry of the digestion medium.

Development of highly faceted reduced graphene oxide-coated copper oxide and copper nanoparticles on a copper foil surface.

This work describes the formation of reduced graphene oxide-coated copper oxide and copper nanoparticles (rGO-Cu2ONPs, rGO-CuNPs) on the surface of a copper foil supporting graphene oxide (GO) at annealing temperatures of 200-1000 °C, under an Ar atmosphere. These hybrid nanostructures were developed from bare copper oxide nanoparticles which grew at an annealing temperature of 80 °C under nitrogen flux. The predominant phase as well as the particle size and shape strongly depend on the process temperature. Characterization with transmission electron microscopy and scanning electron microscopy indicates that Cu or Cu2O nanoparticles take rGO sheets from the rGO network to form core-shell Cu-rGO or Cu2O-rGO nanostructures. It is noted that such ones increase in size from 5 to 800 nm as the annealing temperature increases in the 200-1000 °C range. At 1000 °C, Cu nanoparticles develop a highly faceted morphology, displaying arm-like carbon nanorods that originate from different facets of the copper crystal structure.

Optical and structural characterization of oleic acid-stabilized CdTe nanocrystals for solution thin film processing.

This work presents results of the optical and structural characterization of oleic acid-stabilized cadmium telluride nanocrystals (CdTe-NC) synthesized by an organometallic route. After being cleaned, the CdTe-NC were dispersed in toluene to obtain an ink-like dispersion, which was drop-cast on glass substrate to deposit a thin film. The CdTe-NC colloidal dispersion as well as the CdTe drop-cast thin films were characterized with regard to the optical and structural properties. TEM analysis indicates that the CdTe-NC have a nearly spherical shape (3.5 nm as mean size). Electron diffraction and XRD diffraction analyses indicated the bulk-CdTe face-centered cubic structure for CdTe-NC. An additional diffraction line corresponding to the octahedral Cd3P2 was also detected as a secondary phase, which probably originates by reacting free cadmium ions with trioctylphosphine (the tellurium reducing agent). The Raman spectrum exhibits two broad bands centered at 141.6 and 162.3 cm(-1), which could be associated to the TO and LO modes of cubic CdTe nanocrystals, respectively. Additional peaks located in the 222 to 324 cm(-1) range, agree fairly well with the wavenumbers reported for TO modes of octahedral Cd3P2.