X-ray Free Electron Laser-Induced Synthesis of ε-Iron Nitride at High Pressures.

The ultrafast synthesis of ε-Fe3N1+x in a diamond-anvil cell (DAC) from Fe and N2 under pressure was observed using serial exposures of an X-ray free electron laser (XFEL). When the sample at 5 GPa was irradiated by a pulse train separated by 443 ns, the estimated sample temperature at the delay time was above 1400 K, confirmed by in situ transformation of α- to γ-iron. Ultimately, the Fe and N2 reacted uniformly throughout the beam path to form Fe3N1.33, as deduced from its established equation of state (EOS). We thus demonstrate that the activation energy provided by intense X-ray exposures in an XFEL can be coupled with the source time structure to enable exploration of the time-dependence of reactions under high-pressure conditions.

Intense Reactivity in Sulfur-Hydrogen Mixtures at High Pressure under X-ray Irradiation.

Superconductivity near room temperature in the sulfur-hydrogen system arises from a sequence of reactions at high pressures, with X-ray diffraction experiments playing a central role in understanding these chemical-structural transformations and the corresponding S:H stoichiometry. Here we document X-ray irradiation acting as both a probe and as a driver of chemical reaction in this dense hydride system. We observe a reaction between molecular hydrogen (H2) and elemental sulfur (S8) under high pressure, induced directly by X-ray illumination, at photon energies of 12 keV using a free electron laser. The rapid synthesis of hydrogen sulfide (H2S) at 0.3 GPa was confirmed by optical observations, spectroscopic measurements, and microstructural changes detected by X-ray diffraction. These results document X-ray induced chemical synthesis of superconductor-forming dense hydrides, revealing an alternative production strategy and confirming the disruptive nature of X-ray exposure in studies on high-pressure hydrogen chalcogenides, from water to high-temperature superconductors.

Structures of lithium-zinc compounds at high pressures.

Intermetallic lithium compounds have found a wide range of applications owing to their light mass and desirable electronic and mechanical properties. Here, by compressing pure lithium and zinc mixtures in a diamond-anvil cell, we observe a direct reaction forming the stoichiometric compound LiZn, at pressures below 1 GPa. On further compression above 10 GPa, we observe the formation of Li2Zn, which is the highest lithium content compound to be discovered in the Li-Zn system. Our results constrain the structures of these compounds and their evolution with pressure, furthering our understanding of potentially useful light volume-efficient energy storage materials.

Synthesis and stability of hydrogen selenide compounds at high pressure.

The observation of high-temperature superconductivity in hydride sulfide (H2S) at high pressures has generated considerable interest in compressed hydrogen-rich compounds. High-pressure hydrogen selenide (H2Se) has also been predicted to be superconducting at high temperatures; however, its behaviour and stability upon compression remains unknown. In this study, we synthesize H2Se in situ from elemental Se and molecular H2 at pressures of 0.4 GPa and temperatures of 473 K. On compression at 300 K, we observe the high-pressure solid phase sequence (I-I'-IV) of H2Se through Raman spectroscopy and x-ray diffraction measurements, before dissociation into its constituent elements. Through the compression of H2Se in H2 media, we also observe the formation of a host-guest structure, (H2Se)2H2, which is stable at the same conditions as H2Se, with respect to decomposition. These measurements show that the behaviour of H2Se is remarkably similar to that of H2S and provides further understanding of the hydrogen chalcogenides under pressure.