Structure, morphology, adhesion and in vitro biological evaluation of antibacterial multi-layer HA-Ag/SiO2/TiN/Ti coatings obtained by RF magnetron sputtering for biomedical applications.

Biocompatible and antibacterial multi-layer coatings of hydroxyapatite (HA)-Ag/SiO2/TiN/Ti were obtained on the Ti-6Al-4V alloy, by means of the magnetron sputtering technique. During characterization of the coatings, the chemical composition was evaluated by energy dispersive X-ray spectroscopy and the phase analysis was carried out by X-ray diffraction. The morphology of the coatings was observed by field emission scanning electron microscopy, while transmission electron microscopy was used to appreciate their structure. The adhesion of the coatings to the substrate was evaluated by micro scratch test. The in vitro biological response was evaluated in terms of cytotoxicity, adhesion and differentiation of mouse mesenchymal stem cells, as well as adhesion and bacterial viability of Staphylococcus aureus strain. Through the compositional study carried out, the deposition of the HA phase was verified, with a Ca/P ratio close to 1.67 and the characteristic diffraction peaks of this compound. The structural study of the coatings evidenced the obtention of multi-layer architectures. The use of an intermediate SiO2/TiN/Ti trilayer was found to improve adhesion between HA-Ag and the substrate by 84%. Finally, the in vitro biological tests carried out indicated a potentially non-toxic character in the coatings. Additionally, an antibacterial effect was registered at low concentrations of Ag (<0.25 mg/L).

Antibacterial effect of novel biodegradable and bioresorbable PLDA/Mg composites.

Polylactic acid/Mg composites have been recently proposed for biodegradable osteosynthesis devices because, with regards to the neat polymer, they combine an enhanced biocompatibility and bioactivity with better mechanical properties, particularly creep strength. A question still arises about their bacterial behavior. For this purpose, composites of poly-L-D-lactic acid (PLDA) loaded with 1 and 10 wt.% of Mg microparticles were evaluated using Staphylococcus epidermidis, with special emphasis on the study of bacterial adhesion and biofilm formation. During biofilm formation the bacteria viability of the composites decreased up to 65.3% with respect to PLDA. These antibacterial properties do not compromise the cytocompatibility of the material as the composites enhanced the viability of mesenchymal stem cells and their osteogenic commitment. These findings provide an important added value to the biodegradable and biocompatible PLDA/Mg composites for the manufacture of osteosynthesis devices.

In vivo bactericidal efficacy of farnesol on Ti6Al4V implants. / Eficacia bactericida in vivo del farnesol sobre implantes de Ti6Al4V.

OBJECTIVE: To evaluate the in vivo anti-staphylococcal bactericidal activity of farnesol on Ti6Al4V surfaces. MATERIAL AND METHODS: An experimental model of infection in biomaterials was developed by inoculation of Staphylococcus aureus ATCC 29213 into the canal of both femurs of 15 Wistar rats. A Ti6Al4V pin impregnated with 30mM of farnesol was inserted into study femur, and a Ti6Al4V control was inserted into the control femur. To evaluate the bactericidal efficacy, a comparison was made between the median of the colony forming units recovered after inoculation in the study group and the control group for different times of euthanasia and inoculum size. RESULTS: The median expressed as Log10 CFU counts obtained with farnesol titanium pin was 4.26, and in control group, it was 4.86, which was statistically significant (P=.001) on applying the Student t test for related samples. The median reduction obtained in farnesol pins relative to the control was 74%. CONCLUSIONS: Treatment with farnesol 30mM on Ti6Al4V pins appears to decrease the rate of colonisation by Staphylococcus aureus.

Effect of UV irradiation on the surface Gibbs energy of Ti6Al4V and thermally oxidized Ti6Al4V.

Thermal oxidation of Ti6Al4V increases the thickness, modifies the structure, and changes the amount of alloying elements of the surface titanium dioxide layer with respect to the spontaneous passive layer of Ti6Al4V. The effects on the surface properties of Ti6Al4V and thermally oxidized Ti6Al4V after different periods of UV irradiation have been studied by measurement of water, formamide, and diiodomethane contact angles. The rate of modification of the water contact angle with the irradiation time is dependent on the surface treatment, but the water adhesion work, after an initial energetic step, follows a similar trend for both. Application of the Young equation together with the van Oss approach allowed evaluation of the surface Gibbs energy of the alloys. Similar to the water adhesion work, the surface Gibbs energy dependence on the irradiation time follows a similar trend for both samples and it is due to the change of the electron-donor parameter of the acid-base component. Also, a linear relationship common for both samples has been obtained between the cosines of the water contact angle and the formamide or diiodomethane contact angle. These facts indicate that the surface modification continuously produced by the UV irradiation is similar all along the process and similar for both samples after an energetic threshold for the thermally oxidized sample. It has been also tested that the hydrophilic-hydrophobic conversion is reversible for Ti6Al4V and Ti6Al4V thermally treated.