Oxidative leaching process with cupric ion in hydrochloric acid media for recovery of Pd and Rh from spent catalytic converters.

The recycling of platinum-group metals from wastes such as autocatalytic converters is getting growing attention due to the scarcity of these precious metals and the market pressure originated by increase of demand in current and emerging applications. Hydrometallurgical treatment of such wastes is an alternative way to the most usual pyrometallurgical processes based on smelter operations. This paper focuses on the development of a leaching process using cupric chloride as oxidising agent, in HCl media, for recovery of palladium and rhodium from a spent catalyst. The chloride media allows the adequate conditions for oxidising and solubilising the metals, as demonstrated by equilibrium calculations based on thermodynamic data. The experimental study of the leaching process revealed that Pd solubilisation is clearly easier than that of Rh. The factors temperature, time, and HCl and Cu(2+) concentrations were significant regarding Pd and Rh leaching, the latter requiring higher factor values to achieve the same results. Leaching yields of 95% Pd and 86% Rh were achieved under optimised conditions (T = 80 °C, t = 4h, [HCl] = 6M, [Cu(2+)] = 0.3M).

A myosin-Va tail fragment sequesters dynein light chains leading to apoptosis in melanoma cells.

Previous studies proposed that myosin-Va regulates apoptosis by sequestering pro-apoptotic Bmf to the actin cytoskeleton through dynein light chain-2 (DLC2). Adhesion loss or other cytoskeletal perturbations would unleash Bmf, allowing it to bind and inhibit pro-survival Bcl2 proteins. Here, we demonstrated that overexpression of a myosin-Va medial tail fragment (MVaf) harboring the binding site for DLC2 dramatically decreased melanoma cell viability. Morphological and molecular changes, including surface blebbing, mitochondrial outer membrane permeabilization, cytochrome-c and Smac release, as well as caspase-9/-3 activation and DNA fragmentation indicated that melanoma cells died of apoptosis. Immobilized MVaf interacted directly with DLCs, but complexed MVaf/DLCs did not interact with Bmf. Overexpression of DLC2 attenuated MVaf-induced apoptosis. Thus, we suggest that, MVaf induces apoptosis by sequestering DLC2 and DLC1, thereby unleashing the pair of sensitizer and activator BH3-only proteins Bmf and Bim. Murine embryonic fibroblasts (MEFs) lacking Bim and Bmf or Bax and Bak were less sensitive to apoptosis caused by MVaf expression than wild-type MEFs, strengthening the putative role of the intrinsic apoptotic pathway in this response. Finally, MVaf expression attenuated B16-F10 solid tumor growth in mice, suggesting that this peptide may be useful as an apoptosis-inducing tool for basic and translational studies.

Leaching behaviour of a galvanic sludge in sulphuric acid and ammoniacal media.

Leaching studies of a sludge produced by the physico-chemical treatment of wastewaters generated by a Ni/Cr plating plant were carried out in both sulphuric acid and ammoniacal media aiming to decide which of them would be the best treatment for this kind of waste material. The dissolution behaviour of some metals (Cu, Ni, Cr and Zn) was studied in order to assure the best metal recovery conditions in subsequent processes by the use of some separation methods such as solvent extraction and precipitation techniques. Therefore, the study here presented deals with the first chemical stage of an integrated treatment process. For the sulphuric acid leaching, maximal conversions obtained were 88.6% Cu, 98.0% Ni and 99.2% Zn for the following experimental conditions: a 100 g L(-1) acid concentration, a 5:1 liquid-to-solid ratio (L/S), a particle size less than 1 mm, a digestion time of 1h, a stirring speed of 700 rpm (all at room temperature and under atmospheric pressure). As expected, no selectivity was achieved for the sulphuric acid leaching, despite this option yielding much higher metal ion dissolution when compared with that reached by ammoniacal leaching. The use of this latter medium allowed the extraction of Cu and Ni without Cr species, but rates of conversion were only about 70% for Cu and 50% for Ni, much lower than those obtained for sulphuric acid leaching.

Solvent extraction applied to the recovery of heavy metals from galvanic sludge.

In this study, a hydrometallurgical treatment involving the solvent extraction and recovery of some heavy metals from a sulphuric acid leach solution of galvanic sludge, using di-(2-ethylhexyl)-phosphoric acid (D2EHPA) and bis-(2,4,4-trimethylpentyl)-phosphinic acid (Cyanex 272), both diluted in kerosene, has been investigated. The preliminary tests revealed the necessity to remove other metal species than zinc and nickel, contained in the leach solution, and therefore, processes to cement copper and precipitate chromium were then applied to finally obtain a Zn and Ni pregnant solution prior to solvent extraction. For the experimental conditions studied, Cyanex 272 showed a good recovery of Zn after the stripping stage using H2SO4, but D2EHPA effectively promoted a higher Zn extraction than Cyanex 272 did. The dependence of the solvent extraction method on variables such as pH, contact time and concentration of extractant, as well as the effect of different concentrations of sulphuric acid on stripping, are discussed. The discussion also includes the previous conditions developed to separate the main interfering metallic species from the leach solution in order to improve the extraction and recovery of zinc by solvent extraction. The final objective has been to achieve a solution as pure as possible to recover nickel sulphate.

Towards an understanding of solvent extraction--electroanalytical characterization of chloride-leaching solutions.

Solvent extraction has been employed to purify media simulating chloride-leaching solutions resulting from complex sulfide concentrate processing, and cyclic voltammetry (CV) has been chosen to characterize those hydrometallurgical aqueous phases. The possibilities of the CV technique were investigated by the evaluation of the adequacy of a specific organic extractant, triisobutylphosphine sulfide, aimed to efficiently and selectively extract silver from a complex chloride medium, additionally containing tenfold to 40-fold molar concentrations of iron, copper and lead. The influence of the oxidation state of the metallic ions present in the feed solution, namely Cu(II) and Cu(I), is considered. The possibilities of CV analysis for the characterization of stripping solutions are also illustrated.