The effect of natural aging on the stress corrosion cracking (SCC) of A201-T7 alloy was investigated by the slow strain rate testing (SSRT), transmission electron microscopy (TEM), scanning electron microscopy (SEM), differential scanning calorimetry (DSC), conductivity, and polarization testing. The results indicated that natural aging could significantly improve the resistance of the alloys to SCC. The ductility loss rate of the unaged alloy was 28%, while the rates for the 24 h and 96 h aged alloys were both 5%. The conductivity of the as-quenched alloy was 30.54 (%IACS), and the conductivity of the 24 h and 96 h aged alloys were decreased to 28.85 and 28.65. After T7 tempering, the conductivity of the unaged, 24 h, and 96 h aged alloys were increased to 32.54 (%IACS), 32.52 and 32.45. Besides, the enthalpy change of the 24 h and 96 h aged alloys increased by 36% and 37% compared to the unaged alloy. The clustering of the solute atoms would evidently be enhanced with the increasing time of natural aging. Natural aging after quenching is essential to improve the alloy's resistance to SCC. It might be due to the prevention of the formation of the precipitation free zone (PFZ) after T7 tempering.
RESUMO
The aim of this study is to explore the effects of Manganese addition and homogenization treatment on the microstructures and mechanical properties of the Al-7Mg-0.15Ti (B535.0) alloy. The optical microscopy, electrical conductivity measurements, transmission electron microscopy, scanning electron microscopy (SEM + EBSD), as well as Rockwell hardness and tensile tests, were exploited for this purpose. The main objectives are to refine the grain size, inhibit grain growth in the annealed state, and enhance the mechanical strength of the alloy. The results show that the addition of manganese to the Al-7Mg-0.15Ti alloys refined the as-cast and recrystallized grains of the alloys. During the homogenization process, Al4Mn high-temperature stable dispersoids were precipitated in the aluminum matrix. After annealing, the Al4Mn particles blocked the movement of grain boundaries during the growth of the recrystallized grains and inhibited grain growth. Consequently, the annealed alloys showed grain refinement and dispersion strengthening. The Al4Mn dispersoids of the alloys with manganese added were smaller and denser after a two-stage homogenization process compared to those that underwent a one-stage homogenization process. By contrast, for the alloys without the addition of manganese, the recrystallized grains showed normal growth after annealing, and different homogenization processes had no significantly different effects.