In the present paper, the cyclic stability of the high-temperature two-way shape memory effect was studied in high-strength Ni50.3Ti32.2Hf17.5 polycrystals after various thermomechanical treatments-training (thermocycling under stress) and stress-induced martensite aging. The effect of training and stress-induced martensite aging on the microstructure, the two-way shape memory effect, and its cyclic stability was determined. It was found out that both thermomechanical treatments induce the high-temperature two-way shape memory effect at T > 373 K, with a strain of 1.5% in tension. The influence of cyclic tests (up to 100 stress-free cycles of cooling/heating) on the two-way shape memory effect strain, the transformation temperatures, and the microstructure was established. Different degradation mechanisms of the two-way shape memory effect were established after thermocycling and stress-induced martensite aging.
RESUMO
Measurements have been carried out to compare stress-induced martensite stabilization aged (SIM-aged) and as grown shape memory Ni53Mn25Ga22 single crystals with the means of simultaneous differential scanning calorimetry (DSC) and acoustic emission (AE). Contrary to expectations, the position of the hysteresis practically did not change, whilst the width of the hysteresis increased, and the forward and reverse transitions became sharper in the SIM-aged sample. The energy distributions of acoustic hits showed regular power law behaviour and the energy exponents were slightly different for heating and cooling; this asymmetry had different signs for the SIM-aged and as grown samples. During heating, in accordance with the sharper transitions observed in the DSC runs, two well-marked jumps could be seen on the plot of cumulative number of the acoustic emission events. Therefore, these were attributed to high sudden jumps in the phase transition during heating observed in the DSC. The effect of the SIM-aging on the transformation entropy was also investigated and it was found that it was about 36% less in the case of the SIM-aged sample.