Rapid Microwave-Assisted Synthesis of N/TiO2/rGO Nanoparticles for the Photocatalytic Degradation of Pharmaceuticals.

Nanocomposites comprising nitrogen-doped TiO2 and reduced graphene oxide (N/TiO2/rGO), with different rGO loading qualities, were prepared by a cost-effective microwave-assisted synthesis method. The synthesized materials were broadly characterized by Raman spectroscopy, X-ray diffraction (XRD), infrared spectroscopy (FTIR), photoelectron spectroscopy (XPS), diffuse reflectance spectroscopy (DRS), electron microscopy (SEM-EDS), and nitrogen adsorption/desorption isotherms. Anatase was the only crystalline phase observed for all synthesized materials. The rGO loading did not affect the morphological properties, but it positively influenced the photocatalytic activity of the nanocomposite materials, especially at low rGO loading. Photocatalysts were evaluated via the degradation of specific organic micropollutant (OMP) pharmaceuticals: ciprofloxacin (CIP), diclofenac (DCF), and salicylic acid (SA), under different radiation sources: ultraviolet A (UVA), solar light simulator (SLS), blue visible light (BVL) and cold visible light (CVL). CIP and SA were removed effectively via the synergy of adsorption and photocatalysis, while DCF degradation was achieved solely by photocatalysis. After implementing scavenger agents, photocatalytic degradation processes mainly depended on the specific pollutant type, while irradiation sources barely defined the photocatalytic mechanism. On the other hand, changes in irradiation intensity significantly influenced the photolysis process, while photocatalysis was slightly affected, indicating that irradiation spectra are more relevant than intensity.

Microwave-Assisted Synthesis of N/TiO2 Nanoparticles for Photocatalysis under Different Irradiation Spectra.

Nitrogen-doped TiO2 (N/TiO2) photocatalyst nanoparticles were derived by the environmentally friendly and cost-effective microwave-assisted synthesis method. The samples were prepared at different reaction parameters (temperature and time) and precursor ratio (amount of nitrogen source; urea). The obtained materials were characterized by X-ray diffraction (XRD), photoelectron spectroscopy (XPS), Raman spectroscopy (RS), infrared spectroscopy (FTIR), diffuse reflectance spectroscopy (DRS), electron microscopy (SEM-EDS), and nitrogen adsorption/desorption isotherms. Two cycles of optimizations were conducted to determine the best reaction temperature and time, as well as N content. The phase composition for all N/TiO2 nanomaterials was identified as photoactive anatase. The reaction temperature was found to be the most relevant parameter for the course of the structural evolution of the samples. The nitrogen content was the least relevant for the development of the particle morphology, but it was important for photocatalytic performance. The photocatalytic activity of N/TiO2 nanoparticle aqueous suspensions was evaluated by the degradation of antibiotic ciprofloxacin (CIP) under different irradiation spectra: ultraviolet A light (UVA), simulated solar light, and visible light. As expected, all prepared samples demonstrated efficient CIP degradation. For all irradiation sources, increasing synthesis temperature and increasing nitrogen content further improved the degradation efficiencies.

Synthesis and Nanoarchitectonics of Novel Squaraine Derivatives for Organic Photovoltaic Devices.

Necessary advancements in the area of organic photovoltaic (OPV) devices include the upgrade of power conversion efficiencies (PCE) and stability. One answer to these demands lies in the research into new absorbers. Here, we focus on the development of new small molecule absorbers from the group of squaraines (SQs). These modular absorbers can be applied as donors in organic solar cells and have the ability to utilize a broad range of solar radiation if blended with suitable acceptors. In order to allow for the compatibility and favorable organization of donor and acceptor in the absorber layer, we intend to optimize the structure of the SQ by varying the groups attached to the squaric acid core. For that purpose, we accordingly developed a well-suited synthesis route. The novel alkyl- and benzyl-substituted aryl aminosquaraines were synthesized through an improved and eco-friendly procedure. Special emphasis was placed on optimizing the amination reaction to obtain initial precursors in the synthesis of squaraine, avoiding hitherto common catalytic processes. All SQ precursors and SQ products were completely described. The derived SQs were additionally characterized in thin-film configuration using cyclic voltammetry and UV-VIS spectroscopy and then processed to prepare self-standing bulk heterojunction (BHJ) thin films in conjunction with fullerene-based electron acceptors, which were characterized via profilometry. The comparison between SQ and BHJ solutions and thin films, using atomic force microscopy and UV-VIS spectroscopy, revealed differences in susceptibility for the organization and orientation of the constituting domains.

Humidity Sensing Ceria Thin-Films.

Lowering the constitutive domains of semiconducting oxides to the nano-range has recently opened up the possibility of added benefit in the research area of sensing materials, in terms both of greater specific surface area and pore volume. Among such nanomaterials, ceria has attracted much attention; therefore, we chemically derived homogeneous ceria nanoparticle slurries. One set of samples was tape-casted onto a conducting glass substrate to form thin-films of various thicknesses, thereby avoiding demanding reaction conditions typical of physical depositions, while the other was pressed into pellets. Structural and microstructural features, along with electrical properties and derivative humidity-sensing performance of ceria thin-films and powders pressed into pellets, were studied in detail. Particular attention was given to solid-state impedance spectroscopy (SS-IS), under controlled relative humidity (RH) from 30%-85%, in a wide temperature and frequency range. Moreover, for the thin-film setup, measurements were performed in surface-mode and cross-section-mode. From the results, we extrapolated the influence of composition on relative humidity, the role of configuration and thin-film thickness on electrical properties, and derivative humidity-sensing performance. The structural analysis and depth profiling both point to monophasic crystalline ceria. Microstructure analysis reveals slightly agglomerated spherical particles and thin-films with low surface roughness. Under controlled humidity, the shape of the conductivity spectrum stays the same along with an increase in RH, and a notable shift to higher conductivity values. The relaxation is slow, as the thickness of the pellet slows the return of conductivity values. The increase in humidity has a positive effect on the overall DC conductivity, similar to the temperature effect for semiconducting behavior. As for the surface measurement setup, the thin-film thickness impacts the shape of the spectra and electrical processes. The surface measurement setup turns out to be more sensitive to relative humidity changes, emphasized with higher RH, along with an increase in thin-film thickness. The moisture directly affects the conductivity spectra in the dispersion part, i.e., on the localized short-range charge carriers. Moisture sensitivity is a reversible process for thin-film samples, in contrast to pellet form samples.

Structural and Electrical Characterization of Pure and Al-Doped ZnO Nanorods.

Pure and Al-doped (3 at.%) ZnO nanorods were prepared by two-step synthesis. In the first step, ZnO thin films were deposited on silicon wafers by spin coating; then, ZnO nanorods (NR) and Al-doped ZnO NR were grown using a chemical bath method. The structural properties of zincite nanorods were determined by X-ray diffraction (XRD) and corroborated well with the morphologic properties obtained by field-emission gun scanning electron microscopy (FEG SEM) with energy-dispersive X-ray spectroscopy (EDS). Morphology results revealed a minute change in the nanorod geometry upon doping, which was also visible by Kelvin probe force microscopy (KPFM). KPFM also showed preliminary electrical properties. Detailed electrical characterization of pure and Al-doped ZnO NR was conducted by temperature-dependent current-voltage (I-V) measurements on Au/(Al)ZnO NR/n-Si junctions. It was shown that Al doping increases the conductivity of ZnO NR by an order of magnitude. The I-V characteristics of pure and Al-doped ZnO NR followed the ohmic regime for lower voltages, whereas, for the higher voltages, significant changes in electric conduction mechanisms were detected and ascribed to Al-doping. In conclusion, for future applications, one should consider the possible influence of the geometry change of (Al)ZnO NRs on their overall electric transport properties.

In-Operando Diffraction and Spectroscopic Evaluation of Pure, Zr-, and Ce-Doped Vanadium Dioxide Thermochromic Films Derived via Glycolate Synthesis.

Pure and doped vanadia (VO2, V0.98Zr0.02O2, V0.98Ce0.02O2) samples were prepared by wet chemistry synthesis from vanadyl glycolate intermediate phase and tape casted into films. Combining in-operando grazing incidence synchrotron X-ray diffraction and Raman spectroscopy, we studied the structural evolution of the films under isothermal conditions. The setup allowed assessment of the thermochromic functionality with continuous monitoring of the monoclinic to tetragonal transition in pure and doped vanadia phases, responsible for the transmission and reflection of light in the infrared part of the solar spectrum. The materials characterisation by X-ray diffraction beamline (MCX) goniometer demonstrated ideal performance, combining flexible geometry, high resolution, and the potential to accommodate the multi-channel equipment for in-operando characterisation. This method proved viable for evaluating the relevant structural and physical, and thereof functional properties of these systems. We revealed that dopants reduce the transition temperature by 5 °C on average. The synthetic route of the films was held responsible for the observed phase separation. The more favourable behaviour of cerium-doped sample was attributed to cerium alkoxide behaviour. In addition, structural, microstructural, thermal, and spectroscopic characterisation on powder samples was performed to gain more insight into the development of the phases that are responsible for thermochromic features in a broader range of doping ratios. The influence of the dopants on the extent of the thermochromic transition (transmission to reflection hysteresis) was also evaluated using (micro) structural, thermal and spectroscopic methods of powder samples. Characterisations showed that zirconium doping in 2, 4, and 6 mol% significantly influenced the phase composition and morphology of the precursor. Vanadium oxides other than VO2 can easily crystallise; however, a thermal treatment regime that allowed crystallisation of VO2 as a single phase was established.

ZnO@TiO2 Core Shell Nanorod Arrays with Tailored Structural, Electrical, and Optical Properties for Photovoltaic Application.

ZnO has prominent electron transport and optical properties, beneficial for photovoltaic application, but its surface is prone to the formation of defects. To overcome this problem, we deposited nanostructured TiO2 thin film on ZnO nanorods to form a stable shell. ZnO nanorods synthesized by wet-chemistry are single crystals. Three different procedures for deposition of TiO2 were applied. The influence of preparation methods and parameters on the structure, morphology, electrical and optical properties were studied. Nanostructured TiO2 shells show different morphologies dependent on deposition methods: (1) separated nanoparticles (by pulsed laser deposition (PLD) in Ar), (2) a layer with nonhomogeneous thickness (by PLD in vacuum or DC reactive magnetron sputtering), and (3) a homogenous thin layer along the nanorods (by chemical deposition). Based on the structural study, we chose the preparation parameters to obtain an anatase structure of the TiO2 shell. Impedance spectroscopy shows pure electron conductivity that was considerably better in all the ZnO@TiO2 than in bare ZnO nanorods or TiO2 layers. The best conductivity among the studied samples and the lowest activation energy was observed for the sample with a chemically deposited TiO2 shell. Higher transparency in the visible part of spectrum was achieved for the sample with a homogenous TiO2 layer along the nanorods, then in the samples with a layer of varying thickness.