Vapor-transport equilibrated near-stoichiometric lithium tantalate for frequency-conversion applications.

Near-stoichiometric lithium tantalate (SLT) crystals were produced from congruent lithium tantalate by a vapor-transport equilibration process. Because of the resultant increase in photoconductivity and reduction in photogalvanism, the crystals showed no observable photorefractive damage at 514.5 nm up to the highest intensity used, 2 MW/cm2. The crystals also exhibited low green-induced infrared absorption, a Curie temperature of 693 degrees C, and a coercive field of 80 V/mm. The SLT samples were periodically poled with an 8-microm-period grating, permitting first-order quasi-phase-matched second-harmonic generation of 532-nm radiation at 43 degrees C. A 17-mm-long sample generated 1.6 W of continuous-wave output power at 532 nm for 50 h. With 150-ns pulses at a 100-kHz repetition rate in the same sample, 5-W average-power, 532-nm radiation was generated for 1000 h. No damage to the crystal and no aging effects were observed during these experiments.

Direct imaging of multimode interference in a channel waveguide.

By use of a near-field scanning optical microscope in collection mode, multimode interference was directly measured in an annealed proton-exchanged LiNbO3 waveguide. Periodic transitions from a single-peaked Gaussianlike intensity distribution to a double-peaked intensity distribution were observed. The intensity distribution along the waveguide was calculated, and the results agree well with the experimental observation.

Difference frequency generation of 8-microm radiation in orientation- patterned GaAs.

First-order quasi-phase-matched difference frequency generation of narrowband tunable mid-infrared light is demonstrated in orientation-patterned GaAs. The all-epitaxial orientation-patterned crystal is fabricated by a combination of molecular beam epitaxy and hydride vapor phase epitaxy. Lasers at 1.3 and 1.55 microm were mixed to give an idler output at 8 microm, with power and wavelength tuning consistent with theoretical estimates, indicating excellent material uniformity over the 19-mm-long and 500-microm-thick device.

Optical-frequency balanced mixer.

Optical signal processing devices based on quasi-phase-matched three-wave mixing and cascaded three-wave mixing in guided-wave geometries have been demonstrated to operate efficiently at practical pump-power levels. We describe operation of such devices in a balanced mode that allows mixing without wavelength offset and separation of mixed output from pump and signal input without wavelength-selective filters. We present a design for an optical-frequency balanced mixer using quasi-phase-matched, cascaded second-order nonlinear processes. Using this design, we fabricated a balanced mixer in periodically poled lithium niobate waveguides that has the expected linear and nonlinear optical performance.

Multiple-channel wavelength conversion by use of engineered quasi-phase-matching structures in LiNbO(3) waveguides.

We report difference frequency generation-based wavelength converters with multiple phase-matching wavelengths that use engineered quasi-phase-matching structures in LiNbO(3) waveguides. Multiple-channel wavelength conversion is demonstrated within the 1.5-mum band and between the 1.3- and 1.5-mum bands. With simultaneous use of M pump wavelengths, these devices can also be used to perform wavelength broadcasting, in which each of N input signals is converted into M output wavelengths.

Nonlinear directional coupler in periodically poled lithium niobate.

Nonlinear wave propagation was investigated experimentally in coupled waveguides by means of the cascaded nonlinearity in quasi-phase-matched second-harmonic generation. With a specially designed wave-vector-mismatch distribution along the propagation axis, cascading was optimized for low fundamental depletion. High-contrast, ultrafast all-optical switching with switching powers of tens of watts was observed.