RESUMO
In this research, the physical, mechanical and morphological properties of oil palm empty fruit bunch (EFB) mat/woven kenaf fabric-reinforced epoxy composites have been investigated. The oil palm EFB/woven kenaf fabrics were varied, with weight ratios of 50/0 (T1), 35/15 (T2), 25/25 (T3), 15/35 (T4) and 0/50 (T5). The composites were fabricated using a simple hand lay-up technique followed by hot pressing. The result obtained shows that an increase in kenaf fiber content exhibited higher tensile and flexural properties. On the other hand, the opposite trend was observed in the impact strength of hybrid composites, where an increase in kenaf fiber content reduced the impact strength. This can be corroborated with the physical properties analysis, where a higher void content, water absorption and thickness swelling were observed for pure oil palm EFB (T1) composites compared to other samples. The scanning electron microscopy analysis results clearly show the different failure modes of the tensile fractured samples. Statistical analysis was performed using one-way ANOVA and shows significant differences between the obtained results.
RESUMO
The production of bioadsorbent from palm kernel shell (PKS) and coconut shell (CS) pretreated with 30% phosphoric acid (H3PO4) was optimized using the response surface methodology (RSM). Iodine adsorption for both bioadsorbents was optimized by central composite design. Two parameters including the H3PO4 pretreatment temperature and carbonization temperature were determined as significant factors to improve the iodine adsorption of the bioadsorbent. Statistical analysis results divulge that both factors had significant effect on the iodine adsorption for the bioadsorbent. From the RSM analysis, it was suggested that using 80 and 79°C as H3PO4 pretreatment temperature and 714 and 715°C as carbonization temperature would enhance the iodine adsorption of the CS and PKS bioadsobent, respectively. These results indicated that H3PO4 is a good pretreatment for preparing PKS and CS prior to carbonization process to produce bioadsorbent with well-developed microporous and mesoporous volume. The effort to produce alternative high grade and inexpensive adsorbent derived from lignocellulosic biomass, particularly in the nut shell form was implied in this research.
RESUMO
In the present study, agricultural biomass-palm kernel shell (PKS) and coconut shell (CS)-was used to produce high porosity bioadsorbent using two-stage continuous physical activation method with different gas carrier (air and N2) in each stage. The activation temperature was set constant at 600, 700, 800 or 900°C for both activation stages with the heating rate of 3°C min-1. Two parameters, the gas carrier and activation temperature, were determined as the significant factors on the adsorption properties of bioadsorbent. BET, SEM, FTIR, TGA, CHNS/O and ash content were used to elucidate the developed bioadsorbent prepared from PKS and CS and its capacity towards the adsorption of methylene blue and iodine. The novel process of two-stage continuous physical activation method was able to expose mesopores and micropores that were previously covered/clogged in nature, and simultaneously create new pores. The synthesized bioadsorbents showed that the surface area (PKS: 456.47 m2 g-1, CS: 479.17 m2 g-1), pore size (PKS: 0.63 nm, CS: 0.62 nm) and pore volume (PKS: 0.13 cm3 g-1, CS: 0.15 cm3 g-1) were significantly higher than that of non-treated bioadsorbent. The surface morphology of the raw materials and synthesized bioadsorbent were accessed by SEM. Furthermore, the novel process meets the recent industrial adsorbent requirements such as low activation temperature, high fixed carbon content, high yield, high adsorption properties and high surface area, which are the key factors for large-scale production of bioadsorbent and its usage.