Optically transparent and electrically conductive single-walled carbon nanotube (SWNT) thin films were fabricated at room temperature using a dip-coating technique. The film transparency and sheet resistance can be easily tailored by controlling the number of coatings. Aminopropyltriethoxysilane (APTS) was used as an adhesion promoter and, together with surfactant Triton X-100, greatly improved the SWNTs coating. Only five coats were required to obtain a sheet resistance of 2.05 [Formula: see text] and film transparency of 84 %T. The dip-coated film after post-deposition treatment with nitric acid has a sheet resistance as low as 130 [Formula: see text] at 69 %T. This technique is suitable for large-scale SWNT coating at room temperature and can be used on different types of substrates such as glass and plastics. This paper will discuss the role of the adhesion promoter and surfactant in the coating process.
RESUMO
The excellent shock-absorbing performance of WS2 and MoS2 nanoparticles with inorganic fullerene-like structures (IFs) under very high shock wave pressures of 25 GPa is described. The combined techniques of X-ray diffraction, Raman spectroscopy, X-ray photoelectron spectroscopy, thermal analysis, and transmission electron microscopy have been used to evaluate the diverse, intriguing features of shock recovered IFs, of interest for their tribological applications, thereby allowing improved understanding of their antishock behavior and structure-property relationships. Two possible failure mechanisms are proposed and discussed. The supershock-absorbing ability of the IF-WS2 enables them to survive pressures up to 25 GPa accompanied with concurrent temperatures of up to 1000 degrees C without any significant structural degradation or phase change making them probably the strongest cage molecules now known.