RESUMO
To evaluate the fracture strength and the failure mode of endodontically treated molars restored with monolithic lithium disilicate and zirconia endocrowns and overlays. A total of 48 extracted mandibular molars were endodontically treated, decoronated 2 mm above the cementoenamel junction and divided into four 12-specimen groups. Group ELD: lithium disilicate endocrowns. Group EZ: monolithic zirconia endocrowns. Group OLD: lithium disilicate overlays. Group OZ: monolithic zirconia overlays. Overlays did not extend in the pulp chamber and endocrowns extended in the pulp chamber 2 mm. After adhesive bonding of the restorations, the specimens were subjected to thermocycling (×5000 cycles) and then to fracture resistance testing at lateral static loading (1 mm/min) at a universal testing machine. The failure mode of the specimens was qualitatively evaluated. Differences in means were compared using with t-tests for independent samples or Mann-Whitney test (p < 0.05). Weibull distribution analysis was also performed. Group ELD showed significantly higher fracture strength than all other groups (p = 0.001), and the highest Weibull modulus. Conclusions: Lithium disilicate endocrowns exhibit higher fracture strength and are more reliable compared to the other types of restorations examined. Endocrowns had more catastrophic failures compared to overlays.