Fe3O4@Gum Arabic modified polyvinyl chloride membranes to improve antifouling performance and separation efficiency of organic pollutants.

Nanofiltration (NF) membranes are promising media for water and wastewater treatment; however, they suffer from their hydrophobic nature and low permeability. For this reason, the polyvinyl chloride (PVC) NF membrane was modified by iron (III) oxide@Gum Arabic (Fe3O4@GA) nanocomposite. First, Fe3O4@GA nanocomposite was synthesized by the co-precipitation approach and then its morphology, elemental composition, thermal stability, and functional groups were characterized by various analyses. Next, the prepared nanocomposite was added to the casting solution of the PVC membrane. The bare and modified membranes were fabricated by a nonsolvent-induced phase separation (NIPS) method. The characteristics of fabricated membranes were assessed by mechanical strength, water contact angle, pore size, and porosity measurements. The optimum Fe3O4@GA/PVC membrane had a 52 L m-2. h-1. bar-1 water flux with a high flux recovery ratio (FRR) value (82%). Also, the filtration experiment exhibited that the Fe3O4@GA/PVC membrane could remarkably remove organic contaminants, achieving high rejection rates of 98% Reactive Red-195, 95% Reactive Blue-19, and 96% Rifampicin antibiotic by 0.25 wt% of Fe3O4@GA/PVC membrane. According to the results, adding Fe3O4@GA green nanocomposite to the membrane casting solution is a suitable and efficient procedure for modifying NF membranes.

Impact of a new functionalization of multiwalled carbon nanotubes on antifouling and permeability of PVDF nanocomposite membranes for dye wastewater treatment.

Here, novel hydroxyl and carboxyl functionalized multiwalled carbon nanotubes (AHF-MWCNT and ACF-MWCNT) were successfully synthesized and introduced for modification and antifouling improvement of the PVDF membrane. The blending effect of AHF-MWCNT and ACF-MWCNT on the morphology and surface properties of the PVDF membrane was explored by SEM, AFM, water contact angle, and zeta potential analysis. The results indicated that the membrane surface has become more hydrophilic, smoother as well more negative. In addition, the overall porosity and mean pore radius are increased by MWCNTs embedding. The filtration performance, antifouling and dye separation of the nanocomposite membranes were improved by adding any amounts of AHF-MWCNT and ACF-MWCNT in the PVDF membrane matrix. The carboxylic modification presented better performance than the hydroxyl functionalization. The 0.1 wt% ACF-MWCNT blended membrane presented an optimum performance with 46 L m-2 h-1 bar-1 permeability, 93% FRR, and 97.3% dye rejection. Consequently, embedding functionalized MWCNT in the PVDF membrane matrix was led to improvement of membrane characteristics and enhancement of pure water flux, antifouling feature, and dye separation. So, the functionalized MWCNT could be a promising additive for the PVDF membrane modification.

Highly antifouling polymer-nanoparticle-nanoparticle/polymer hybrid membranes.

We introduce highly antifouling Polymer-Nanoparticle-Nanoparticle/Polymer (PNNP) hybrid membranes as multi-functional materials for versatile purification of wastewater. Nitrogen-rich polyethylenimine (PEI)-functionalized halloysite nanotube (HNT-SiO2-PEI) nanoparticles were developed and embedded in polyvinyl chloride (PVC) membranes for protein and dye filtration. Bulk and surface characteristics of the resulting HNT-SiO2-PEI nanocomposites were determined using Fourier-transform infrared spectroscopy (FTIR), X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), transmission electron microscopy (TEM), and thermogravimetric analysis (TGA). Moreover, microstructure and physicochemical properties of HNT-SiO2-PEI/PVC membranes were investigated by scanning electron microscopy (SEM), atomic force microscopy (AFM), and attenuated total reflectance (ATR)-FTIR. Results of these analyses indicated that the overall porosity and mean pore size of nanocomposite membranes were enhanced, but the surface roughness was reduced. Additionally, surface hydrophilicity and flexibility of the original PVC membranes were significantly improved by incorporating HNT-SiO2-PEI nanoparticles. Based on pure water permeability and bovine serum albumin (BSA)/dye rejection tests, the highest nanoparticle-embedded membrane performance was observed at 2 weight percent (wt%) of HNT-SiO2-PEI. The nanocomposite incorporation in the PVC membranes further improved its antifouling performance and flux recovery ratio (96.8%). Notably, dye separation performance increased up to 99.97%. Overall, hydrophobic PVC membranes were successfully modified by incorporating HNT-SiO2-PEI nanomaterial and better-quality wastewater treatment performance was obtained.

Hydrogen peroxide treated g-C3N4 as an effective hydrophilic nanosheet for modification of polyethersulfone membranes with enhanced permeability and antifouling characteristics.

In this study, first, graphitic carbon nitride was treated with hydrogen peroxide (abbreviated as H2O2-g-C3N4), then was used as a new hydrophilic nanomaterial in the fabrication of polyethersulfone (PES) mixed matrix membrane (MMM) for improving flux, protein and dye separation efficiency and antifouling properties. The H2O2-g-C3N4 nanosheet was inserted into the doping solution to fabricate PES/H2O2-g-C3N4 nanocomposite membrane with the non-solvent induced phase inversion procedure. The results of the SEM and AFM images and also porosity and contact angle analysis were indicated that the modified membranes with H2O2-g-C3N4 had more porosity, smoother surface and more hydrophilic. Also, the influence of various weight percentage of H2O2-g-C3N4 was investigated systematically on the membrane performance. By blending of H2O2-g-C3N4 nanosheet in the membrane matrix, the permeability was raised from 4.1 (for bare membrane) to 30.1 L m-2 h-1 bar-1. Additionally, the effect of the H2O2-g-C3N4 material on the antifouling features indicated that the flux recover ratio of the H2O2-g-C3N4 MMMs was improved and the resistance parameters were reduced. Also, the effect of the H2O2-g-C3N4 material on the antifouling features indicated that the flux recover ratio of the H2O2-g-C3N4 MMMs was improved and the resistance parameters were reduced. Finally, the dye rejection efficiency of the nanocomposite membranes for Orange II and Reactive Yellow 168 was improved. As a result, it could be mentioned that the mixing low amount of H2O2-g-C3N4 in the membrane structure could significantly improve the membrane flux and antifouling properties without reduction in membrane rejection efficiency.