A new type of biodegradable drug-loaded fibre scaffold has been successfully produced for the benefit of water-soluble drugs and proteins. Model drug loaded calcium carbonate (CaCO3) microparticles incorporated into poly(lactic acid-co-glycolic acid) (PLGA) fibres were manufactured by co-precipitation of CaCO3 and the drug molecules, followed by electrospinning of a suspension of such drug-loaded microparticles in a PLGA solution. Rhodamine 6G and bovine serum albumin were used as model drugs for our release study, representing small bioactive molecules and protein, respectively. A bead and string structure of fibres was achieved. The drug release was investigated with different drug loadings and in different pH release mediums. Results showed that a slow and sustained drug release was achieved in 40 days and the CaCO3 microparticles used as the second barrier restrained the initial burst release.
Assuntos
Materiais Biocompatíveis , Preparações Farmacêuticas/química , Proteínas/química , Água/química , Sistemas de Liberação de Medicamentos , Concentração de Íons de Hidrogênio , Cinética , Ácido Láctico/química , Microscopia Eletrônica de Varredura , Microscopia de Fluorescência , Ácido Poliglicólico/química , Copolímero de Ácido Poliláctico e Ácido Poliglicólico , SolubilidadeRESUMO
DC magnetoresistive effects were observed in above-percolation-threshold loaded Fe-filled carbon nanotube/polyurethane-urea composite samples. A phenomenological model is derived from interpretation of resistance relaxation for a range of axial strains. The large instantaneous magnetoresistance of + 90% observed at low axial strain was a result of conduction pathway breaking caused by preferential orientation of the conducting nanotubes perpendicular to the axial current flow: a result of the magnetic torque experienced by the ferromagnetic nanotube core. At large strain the observed large instantaneous change in resistance of - 90% resulted from voltage-driven relaxation in the conducting nanotube network. At high axial strain the competition between voltage-driven relaxation and a magnetic torque gave rise to an oscillatory component of resistance relaxation.
RESUMO
Carbon nanotubes have mechanical properties that are far in excess of conventional fibrous materials used in engineering polymer composites. Effective reinforcement of polymers using carbon nanotubes is difficult due to poor dispersion and alignment of the nanotubes along the same axis as the applied force during composite loading. This paper reviews the mechanical properties of carbon nanotubes and their polymer composites to highlight how many previously prepared composites do not effectively use the excellent mechanical behaviour of the reinforcement. Nanomechanical tests using atomic force microscopy are carried out on simple uniaxially aligned carbon nanotube-reinforced polyvinyl alcohol (PVA) fibres prepared using electrospinning processes. Dispersion of the carbon nanotubes within the polymer is achieved using a surfactant. Young's modulus of these simple composites is shown to approach theoretically predicted values, indicating that the carbon nanotubes are effective reinforcements. However, the use of dispersant is also shown to lower Young's modulus of the electrospun PVA fibres.