RESUMO
We report a Yb3+ heavily doped photonic crystal fiber with 30 µm core diameter manufactured for the first time by an alternative technique. Silica core rods with a diameter of 3 mm and a length of 280 mm were prepared by the sodium-borosilicate glass phase-separation technology. The measurements show that the fiber has an Yb3+ concentration of 22810 ppm by weight, and a resultant absorption of approximately 8.5 dB/m at 976 nm. The Yb3+ ions are distributed throughout the fiber core with an excellent homogeneity. The laser performance demonstrates a high slope efficiency of 64.5% for laser emission at 1033.4 nm and a low power threshold of 3 W within a short fiber length of 1 m. This novel approach provides an alternative means of preparing large active silica rods with high doping levels and excellent material homogeneity for large mode area fibers with complex designs.