RESUMO
Sulfide stress cracking (SSC) failure is a main concern for the pressure vessel steel Q345 used in harsh sour oil and gas environments containing hydrogen sulfide (H2S). Methods used to improve the strength of steel usually decrease their SSC resistance. In this work, a quenching and tempering (Q&T) processing method is proposed to provide higher strength combined with better SSC resistance for hot-rolled Q345 pressure vessel steel. Compared to the initial hot-rolled plates having a yield strength (YS) of ~372 MPa, the Q&T counterparts had a YS of ~463 MPa, achieving a remarkable improvement in the strength level. Meanwhile, there was a resulting SSC failure in the initial hot-rolled plates, which was not present in the Q&T counterparts. The SSC failure was not only determined by the strength. The carbon-rich zone, residual stress, and sensitive hardness in the banded structure largely determined the susceptibility to SSC failure. The mechanism of the property amelioration might be ascribed to microstructural modification by the Q&T processing. This work provides an approach to develop improved strength grades of SSC-resistant pressure vessel steels.
RESUMO
This study investigates the strengthening mechanism and carbide precipitation behavior of medium Mn steel with Nb-Mo microalloy after cyclic quenching and austenite reverse transformation treatment. The results show that the Nb/Mo element not only precipitates (Nb,Mo)C in the grains, hindering the movement of dislocations and increases the strength, but also segregates at the austenite/ferrite grain boundary, thus delaying the transformation from austenite to ferrite. In addition, a large amount of nano-scale cementite is retained after cyclic quenching and austenite reverse transformation, which has a positive effect on the proportion of retained austenite in medium Mn steel. Moreover, the carbides with small size and low Mn content are dissolved, and the decomposed C and Mn content are beneficial to the nucleation of austenite during the intercritical annealing process at a temperature of 690 °C.