Hydroxyethyl Cellulose-Based Hydrogels as Controlled Release Carriers for Amorphous Solid Dispersion of Bioactive Components of Radix Paeonia Alba.

Radix Paeoniae Alba (RPA) has been used extensively in Chinese traditional medicine to treat gastrointestinal disorders, immune-modulating diseases, cancers, and numerous other conditions. A few of its active components include paeoniflorin, albiflorin, lactiflorin, and catechin. However, their therapeutic effectiveness is compromised by poor pharmacokinetic profiles, low oral bioavailability, short half-lives, and poor aqueous solubility. In this study, hydroxyethyl cellulose-grafted-2-acrylamido-2-methylpropane sulfonic acid (HEC-g-AMPS) hydrogels were successfully prepared for the controlled release of Radix Paeonia Alba-solid dispersion (RPA-SD). A total of 43 compounds were identified in RPA-SD using UHPLC-Q-TOF-MS analysis. The hydrogel network formation was confirmed by FTIR, TGA, DSC, XRD, and SEM. Hydrogels' swelling and drug release were slightly higher at pH 1.2 (43.31% swelling, 81.70% drug release) than at pH 7.4 (27.73% swelling, 72.46% drug release) after 48 h. The gel fraction, drug release time and mechanical strength of the hydrogels increased with increased polymer and monomer concentration. Furthermore, the hydrogels were porous (84.15% porosity) and biodegradable (8.9% weight loss per week). Moreover, the synthesized hydrogels exhibited excellent antimicrobial and antioxidative properties.

Synthesis of Gallic Acid-Loaded Chitosan-Grafted-2-Acrylamido-2-Methylpropane Sulfonic Acid Hydrogels for Oral Controlled Drug Delivery: In Vitro Biodegradation, Antioxidant, and Antibacterial Effects.

In this study, chitosan (CS) and 2-acrylamido-2-methylpropane sulfonic acid (AMPS)-based hydrogels were formulated by the free radical polymerization technique for the controlled release of gallic acid. Fourier transform infrared spectroscopy (FTIR) confirmed the successful preparation and loading of gallic acid within the hydrogel network. Differential scanning calorimetry (DSC) and thermogravimetric analysis (TGA) confirmed the increased thermal stability of the hydrogels following the crosslinking and polymerization of chitosan and AMPS. In X-ray diffraction analysis (XRD), the crystallinity of the raw materials decreased, indicating strong crosslinking of the reagents and the formation of a new polymeric network of hydrogels. Scanning electron microscopy (SEM) revealed that the hydrogel had a rough, dense, and porous surface, which is consistent with the highly polymerized composition of the hydrogel. After 48 h, the hydrogels exhibited higher swelling at pH 1.2 (swelling ratio of 19.93%) than at pH 7.4 (swelling ratio of 15.65%). The drug release was analyzed using ultraviolet-visible (UV-Vis) spectrophotometer and demonstrated that after 48 h, gallic acid release was maximum at pH 1.2 (85.27%) compared to pH 7.4 (75.19%). The percent porosity (78.36%) and drug loading increased with the increasing concentration of chitosan and AMPS, while a decrease was observed with the increasing concentration of ethylene glycol dimethyl methacrylate (EGDMA). Crosslinking of the hydrogels increased with concentrations of chitosan and EGDMA but decreased with AMPS. In vitro studies demonstrated that the developed hydrogels were biodegradable (8.6% degradation/week) and had antimicrobial (zone of inhibition of 21 and 16 mm against Gram-positive bacteria Escherichia coli and Staphylococcus aureus as well as 13 mm against Gram-negative bacteria Pseudomonas aeruginosa, respectively) and antioxidant (73% DPPH and 70% ABTS) properties. Therefore, the prepared hydrogels could be used as an effective controlled drug delivery system.