Assessment of the preventive effects of Nd:YAG laser associated with fluoride on enamel caries using optical coherence tomography and FTIR spectroscopy.

OBJECTIVE: This in vitro study characterized and monitored, by Optical Coherence Tomography (OCT) and Fourier Transformed Infrared Spectroscopy (FTIR), the effects of the association of acidulated phosphate fluoride gel (APF-gel) and Nd:YAG (neodymiun:yttrium-aluminum-garnet) laser, as sequencial treatments, in the prevention of incipient enamel caries lesions. METHODS: 120 human enamel samples were randomized into 3 groups (n = 40): APF-gel (1.23% F-, 4 min.); Laser+APF (Nd:YAG laser irradiation-0.6W, 84.9J/cm2, 10Hz, followed by APF-gel); and APF+Laser (APF-gel followed by laser irradiation). The samples were subjected to a 15-day pH-cycling, evaluated by OCT (quantification of optical attenuation coefficient-OAC) and FTIR (analysis of carbonate and phosphate content) before treatments, after treatments, and on the 5th, 10th and 15th days of pH-cycling. The statistical analysis was performed (α = 5%). RESULTS: The Optical Attenuation Coefficient (OAC) assessed by OCT increases with the progression of demineralization, and the Laser+APF presented the highest values of OAC in 10th and 15th days of pH-cycling. Nd:YAG decreased the carbonate content after treatment regardless of the application order of the APF-gel, while APF-gel did not interfere in the composition of enamel. The carbonate content was also changed in the first 5 days of the pH-cycling in all groups. CONCLUSION: Nd:YAG laser irradiation before or after the application of APF-gel did not influence the appearance of incipient caries lesions, showing no synergistic effect. Regardless of the application order of the APF-gel, laser irradiation reduces the carbonate content of the enamel, which also changes during the demineralization process. However, irradiation before the application of APF-gel increased the speed of progression of the lesions, which positively impacts public health as it can prevent caries disease, even in high risk individuals. OCT and FTIR are suitable for assessing this effect.

The lingual enamel morphology and bracket shear bond strength influenced by Nd:YAG laser and aluminum oxide sandblasting preconditioning.

OBJECTIVES: This study aimed to investigate the influence of Nd:YAG laser and aluminum oxide sandblasting on the shear bond strength (SBS) of lingual brackets and to optically analyze the behavior of the enamel morphology. MATERIALS AND METHODS: Thirty-five bovines' incisors teeth were divided into 5 groups (n = 7), according to the surface preconditioning: G1, control group; G2, Nd:YAG laser; G3, laser + aluminum oxide sandblasting (Al2O3); G4, Al2O3; and G5, Al2O3 + laser. All groups had lingual brackets bonded and shear debonded after 72 h. SBS values were analyzed, and the enamel morphology was evaluated by optical coherence tomography (OCT) and scanning electron microscope (SEM), before and after preconditioning surface. The optical attenuation coefficient (α) analysis was obtained from OCT images. Data analysis used the ANOVA test, followed by post hoc Tukey, Kruskal Wallis, and post hoc Dunn tests (significance of 5%). RESULTS: The SBS values presented similarly among groups, but the value of α showed statistical difference (p-value = 0.0124) between G3 and G5 with the others. Optical analyses indicated a melting on the enamel that suffered laser irradiation for G2 and G5 and crystal surface disorganization for G4. Sandblasting partially removes the melting of the laser effect (G3). CONCLUSION: The sandblasting is a dispensable step for bonding lingual brackets, and the melting of the enamel after laser irradiation does not compromise the bracket adhesive resistance. CLINICAL RELEVANCE: The Nd:YAG laser became an interesting tool to prevent caries and decrease prevalence of white spot lesions in orthodontic treatments, without systemic effects in patients with genetic high risks of caries.