Effect of disinfectant solutions on a denture base acrylic resin.

The aim of this study was to evaluate the hardness, roughness and mass loss of an acrylic denture base resin after in vitro exposure to four disinfectant solutions. Forty specimens (Clássico, Brazil) were prepared and randomly assigned to 4 groups n = 10) according to the disinfectant solution: G1: control, stored in distilled water at 37 degrees C; G2: 1% sodium hypochlorite; G3: 2% glutaraldehyde; G4: 4% chlorhexidine. G2 to G4 were immersed for 60 minutes in the disinfectant solution. Measurements were carried out both before and after immersion in the solution. The surface was analyzed with a surface roughness tester (Surfcorder SE 1700 KOZAKALAB), a microdurometer FM-700 (Future Tech) and a scanning electron microscope (DSM 962-ZEISS). Loss of mass was determined with a digital weighing scale. After disinfection procedures, values were analyzed statistically. The acrylic denture base resin may be vulnerable to surface changes after in vitro immersion in the disinfectant solutions studied.

Effect of disinfectant solutions on a denture base acrylic resin

El objetivo de este estudio fue evaluar la microdureza, rugosidad y pérdida de masa de resinas acrílicas para base de dentadura, después de su exposición a soluciones desinfectantes, in vitro. Cuarenta especimenes de resina acrílica para base de dentadura (Clássico, Brasil) fueron confeccionados y asignados randomizadamente a 4 grupos (n=10) según la solución desinfectante: G1: control, almacenado en agua destilada a 37 °C; G2: 1 por ciento hipoclorito de sodio; G3: 2 por ciento Glutaraldehído; G4: 4 por ciento clorhexidina. Los especimenes fueroninmersos por 60 minutos en la solución correspondiente. Posteriormente, los especimenes fueron analizados antes ydespués de cada inmersión usando un rugosímetro (Surfcorder SE 1700 KOZAKALAB), un microdurómetro FM-700 (Future Tech), un microscopio Electrónico de Barrido (MEB) (DSM 962-ZEISS) y una escala digital. Después de los procedimientos de desinfección, los valores promedios obtenidos de cada análisis fueron evaluados estadísticamente. Las resinas para base de dentadura pueden ser vulnerables a los cambios de superficie cuando son inmersos en soluciones desinfectantes.

Effect of disinfectant solutions on a denture base acrylic resin

El objetivo de este estudio fue evaluar la microdureza, rugosidad y pérdida de masa de resinas acrílicas para base de dentadura, después de su exposición a soluciones desinfectantes, in vitro. Cuarenta especimenes de resina acrílica para base de dentadura (Clássico, Brasil) fueron confeccionados y asignados randomizadamente a 4 grupos (n=10) según la solución desinfectante: G1: control, almacenado en agua destilada a 37 °C; G2: 1 por ciento hipoclorito de sodio; G3: 2 por ciento Glutaraldehído; G4: 4 por ciento clorhexidina. Los especimenes fueroninmersos por 60 minutos en la solución correspondiente. Posteriormente, los especimenes fueron analizados antes ydespués de cada inmersión usando un rugosímetro (Surfcorder SE 1700 KOZAKALAB), un microdurómetro FM-700 (Future Tech), un microscopio Electrónico de Barrido (MEB) (DSM 962-ZEISS) y una escala digital. Después de los procedimientos de desinfección, los valores promedios obtenidos de cada análisis fueron evaluados estadísticamente. Las resinas para base de dentadura pueden ser vulnerables a los cambios de superficie cuando son inmersos en soluciones desinfectantes.(AU)

Analysis of tooth enamel after excessive bleaching: a study using scanning electron microscopy and energy dispersive x-ray spectroscopy.

This study assessed alterations on bovine enamel after excessive bleaching. Coronal portions of bovine teeth (n = 30) were sectioned and divided into three groups (n = 10 per group). The coronal parts were further cut incisocervically into two halves. While one half received no bleaching (control), the other half was subjected to either one (group 1), three (group 2), or five bleaching sessions (group 3) with 35% hydrogen peroxide. The enamel surfaces were then analyzed using scanning electron microscopy and energy dispersive x-ray spectroscopy (EDS). Excessive bleaching affected the surface morphology and chemistry of the bovine enamel. EDS analysis showed the highest decrease in calcium ion percentages in groups 2 and 3 when compared to their nonbleached halves. Oxygen and phosphorus percentages were comparable on both the control and bleached enamel, regardless of the number of bleaching sessions. Consecutive bleaching sessions with 35% hydrogen peroxide may lead to morphologic and specific elemental changes when performed in a short period of time. Calcium ion percentages may decrease when this bleaching agent is used for more than one session. Int J Prosthodontics 2010;23:29-32.

Shear bond strength between metal alloy and a ceramic system, submitted to different thermocycling immersion times.

The aim of this study was to evaluate the shear bond strength of Co-Cr and Ni-Cr metal alloys and a specific ceramic, submitted to different thermocycling immersion times. Sixty metal-ceramic specimens were confectioned and standardized in cylindricalformat. Three thermocycling conditions were evaluated: without thermocycling, 3,000 cycles (5 degrees C/55 degrees C+/-1) with 30s of immersion time and 3,000 cycles (5 degrees C/55 degrees C+/-1) with 60s. The shear bond strength was performed in a universal testing machine, using a special device to concentrate the tension at the metal/ceramic interface during the test. The load was applied until fracture of the specimens. The data was statistically analyzed by ANOVA (two-way) and Tukey (p<0.05) test. The results didn't show significant statistic differences between the metal-porcelain combinations. Nevertheless, both metal-ceramic systems submitted to 60s of immersion time showed lower values compared to specimens without thermocycling. It was concluded that the thermocycling immersion time of 1 minute affect the shear bond strength values for the Ni-Cr/porcelain and Cr-Co/porcelain systems.

Shear bond strenght between metal alloy and a ceramic system, submitted to different thermocycling immersion times

El objetivo de este estudio fue evaluar la resistencia a cizallamiento de aleaciones metálicas de Co-Cr y Ni-Cr; con un mismo tipo de cerámica, sometidos a diferentes tiempos de inmersión en el termociclaje. Sesenta especímenes fueron confeccionados de forma standarden formato cilindrico. Tres condiciones de termociclaje fueron evaluadas: sin termociclaje, 3000 ciclos (5ºC/55ºC±1) con 30s y 3.000 ciclos (5ºC/55ºC±1) con 60s de tiempo de inmersión. El ensayo de cizallamiento fue realizado en una máquina universal usando un dispositivo para concentrar la tensión en la interfase metalocerámica durante el test. La carga fue aplicada hasta que ocurra la fractura de los especimenes. La información fue estadísticamente analizada por ANOVA(two-way) y el test de Tukey (p<0,05). Los resultados no mostraron diferencia estadísticamente significante entre las combinaciones metal-porcelana. Sin embargo, ambas combinaciones metalocerámicas sometidas a 60s de tiempo de inmersión mostraron valores más bajos en comparación con los especimenes del grupo sin termociclaje. Fue concluido que el tiempo de inmersión de termociclaje de 1 minuto afectó los valores de resistencia de cizallamiento en los grupos de Ni-Cr/porcelana y Cr-Co/porcelana.