RESUMO
Novel IR-transparent ceramics of erbium-doped Lu2O3-MgO and Sc2O3-MgO composites have been successfully obtained using a combination of glycine-nitrate self-propagating high-temperature synthesis and vacuum hot-pressing methods. Composites have densities greater than 99.5% of those calculated by X-ray diffraction and consist of uniformly distributed submicron grains of magnesium and rare earth oxides. The transmittances of 1.5 mm thick composites are as high as 84.5% and 78.9% at ~5 µm for Er:Lu2O3-MgO and Er:Sc2O3-MgO, respectively. Both composites are favorable matrices for doping with erbium ions, which exhibit intense luminescence in the visible, near, and mid-IR under relevant excitation. The position of the luminescence bands is similar to Er:Lu2O3 and Er:Sc2O3 ceramics; the lifetimes of the 4I13/2 state are 8.85 ± 0.1 ms and 5.7 ± 0.2 ms for 3%Er:Lu2O3-MgO and 3%Er:Sc2O3-MgO, respectively.
RESUMO
This study looked at optimizing the composition of precursors for yttria nanopowder glycine-nitrate self-propagating high-temperature synthesis (SHS). Based on thermodynamic studies, six different precursor compositions were selected, including with excesses of either oxidant or fuel. The powders from the precursors of all selected compositions were highly dispersed and had specific surface areas ranging from 22 to 57 m2/g. They were consolidated by hot pressing (HP) with lithium-fluoride sintering additive and subsequent hot isostatic pressing (HIP). The 1 mm thick HPed ceramics had transmittance in the range of 74.5% to 80.1% @ 1µm, which was limited by optical inhomogeneity due to incomplete evaporation of the sintering additive. Two-stage HIP significantly improves optical homogeneity of the ceramics. It was shown that an excess of oxidizer in the precursor decreases the powders' agglomeration degree, which forms large pore clusters in the ceramics.
RESUMO
Thermo-optical properties of several (Tb1-xYx)2O3 ceramic samples were investigated in this Letter. The linear absorption and thermal conductivity coefficients, as well as the power dependence of thermally induced phase and polarization distortions of laser radiation, were measured. In addition, the effective thermo-optical constants Peff and Qeff were estimated. Thermo-optical properties of the studied ceramics were compared with those of the widely used terbium gallium garnet. It was shown that the material under consideration is highly promising for Faraday isolators operating at high average power laser radiation.
RESUMO
A cycle of works on manufacturing and studying laser and magnetooptical ceramics with a focus on their thermo-optical characteristics performed by the research team is analyzed. Original results that have not been published before such as measurements of the Verdet constant in the Zr:TAG, Re:MgAl2O4, and ZnAl2O4 ceramics are also presented.