RESUMO
A tunable bandgap without doping is highly desirable for applications in optoelectronic devices. Herein, we develop a new method which can tune the bandgap without any doping. In the present research, the bandgap of Fe2O3 nanostructured films is simply tuned by changing the synthesis temperature. The Fe2O3 nanostructured films are synthesized on ITO/glass substrates at temperatures of 1100, 1150, 1200, and 1250 °C using the hot filament metal oxide vapor deposition (HFMOVD) and thermal oxidation techniques. The Fe2O3 nanostructured films contain two mixtures of Fe2+ and Fe3+ cations and two trigonal (α) and cubic (γ) phases. The increase of the Fe2+ cations and cubic (γ) phase with the elevated synthesis temperatures lifted the valence band edge, indicating a reduction in the bandgap. The linear bandgap reduction of 0.55 eV without any doping makes the Fe2O3 nanostructured films promising materials for applications in bandgap engineering, optoelectronic devices, and energy storage devices.
RESUMO
We synthesized one-dimensional (1D) Magnéli-phase nanorods of Mo4O11 using the hot filament metal-oxide vapor deposition technique. The 1D Magnéli-phase Mo4O11 nanorods synthesized at 1000, 1050, 1100, 1150, and 1200 °C contain varying combinations of two orthorhombic (α) and monoclinic (η) phases, and various mixtures of Mo(4+), Mo(5+) and Mo(6+) cations, while those synthesized at a higher temperature look bluer. The shifts of the transmittance maximum and absorbance minimum of the 1D Magnéli-phase Mo4O11 nanorods are inversely and linearly proportional to the elevated temperature, verifying that the bandgaps (Eg) are inversely proportional to the elevated temperature. The bandgap (Eg) of the 1D Magnéli-phase Mo4O11 nanorods can be tuned by simply controlling the synthesis temperature without doping with other materials, giving the 1D Magnéli-phase Mo4O11 nanorods good potential for use in optoelectronic nanodevices and bandgap engineering.