Influence of Post-Consumer Waste Thermoplastic Elastomers Obtained from Used Car Floor Mats on Concrete Properties.

In this paper, the influence of post-consumer thermoplastic elastomer (TPE) additive derived from used car floor mats on the physical and mechanical properties of concrete is presented. Waste elastomer (fractions 0-2 and 2-8 mm) was used as a substitute for sand or fine aggregate in the amount of 2.5, 5.0, 7.5, and 10.0% by weight of cement. For all series, the physical and mechanical properties of concrete (for example, compressive strength, flexural tensile strength, water absorption, density, and frost resistance), as well as its microstructure, were tested. It has been shown that post-consumer elastomer waste from used car floor mats in the amount of 2.5% of cement weight can replace sand and gravel aggregate in concrete without reducing their mechanical strength and without changing their microstructure. The compressive strength (after 28 days) of concretes in which the waste was introduced as a substitute for sand and aggregate was 57.0 and 57.2 MPa, respectively (the strength of the control sample was 57.0 MPa). The use of post-consumer waste in concrete allows for a reduction in the consumption of natural aggregate (the addition of 2.5% of waste material saves natural aggregate approximately 20 kg/m3), which reduces the cost of concrete production and also has a positive impact on the environment (i.e., it saves cost and space in landfills, where currently used car floor mat are deposited).

Properties and Structure of Concretes Doped with Production Waste of Thermoplastic Elastomers from the Production of Car Floor Mats.

This article presents physical and mechanical properties of concrete composites that include waste thermoplastic elastomer (TPE) from the production process of car floor mats. Waste elastomer (2-8 mm fraction) was used as a substitute for fine aggregate in quantities of 2.5, 5.0, 7.5, and 10% of the cement weight. For all series of concrete, the following tests were carried out: compression strength, bending tensile strength, splitting tensile strength, absorbability, density, resistance to water penetration under pressure, frost resistance, and abrasion resistance, according to applicable standards. Moreover, SEM/EDS analysis was carried out on the surface microstructure of synthesized concrete composites. It was proven that the use of production waste from the production process of car floor mats in the quantity of 2.5% does not influence the change of the concrete microstructure and it does not result in the decrease of the mechanical parameters of concrete modified with waste. All concrete modified with the addition of waste meet standards requirements after carrying out 15 cycles of freezing and thawing, and the average decrease in compression strength did not exceed 20%. Adding waste in the quantity of 2.5% allows for limiting the use of aggregate by about 5%, which is beneficial for the natural environment.