Thermal deposition of intact tetrairon(III) single-molecule magnets in high-vacuum conditions.

A tetrairon(III) single-molecule magnet is deposited using a thermal evaporation technique in high vacuum. The chemical integrity is demonstrated by time-of-flight secondary ion mass spectrometry on a film deposited on Al foil, while superconducting quantum interference device magnetometry and alternating current susceptometry of a film deposited on a kapton substrate show magnetic properties identical to the pristine powder. High-frequency electron paramagnetic resonance spectra confirm the characteristic behavior for a system with S = 5 and a large Ising-type magnetic anisotropy. All these results indicate that the molecules are not damaged during the deposition procedure keeping intact the single-molecule magnet behavior.

Self-assembled organic radicals on Au(111) surfaces: a combined ToF-SIMS, STM, and ESR study.

Electron spin resonance (ESR), time-of-flight secondary ion mass spectrometry (ToF-SIMS), and scanning tunneling microscopy (STM) have been used in parallel to characterize the deposition on gold surface of a series of nitronyl nitroxide radicals. These compounds have been specifically synthesized with methyl-thio linking groups suitable to interact with the gold surface to form self-assembled monolayers (SAMs), which can be considered relevant in the research for molecular-based spintronics devices, as suggested in recent papers. The degree of the expected ordering on the surface of these SAMs has been tuned by varying the chemical structure of synthesized radicals. ToF-SIMS has been used to support the evidence of the occurrence of the deposition process. STM has shown the different qualities of the obtained SAMs, with the degree of local order increasing as the degree of freedom of the molecules on the surface is decreased. Finally, ESR has confirmed that the deposition process does not affect the paramagnetic characteristics of radicals and that it affords a complete single-layered coverage of the surface. Further, the absence of angular dependence in the spectra indicates that the small regions of local ordering do not give rise to a long-range order and suggests a quite large mobility of the radical on the surface, probably due to the weak interaction with gold provided by the methyl-thio linking group.

Advances in single-molecule magnet surface patterning through microcontact printing.

We present an implementation of strategies to deposit single-molecule magnets (SMMs) using microcontact printing microCP). We describe different approaches of microCP to print stripes of a sulfur-functionalized dodecamanganese (III, IV) cluster on gold surfaces. Comparison by atomic force microscopy profile analysis of the patterned structures confirms the formation of a chemically stable single layer of SMMs. Images based on chemical contrast, obtained by time-of-flight secondary ion mass spectrometry, confirm the patterned structure.

Role of the Hyal-Cu (II) complex on bovine aortic and lymphatic endothelial cells behavior on microstructured surfaces.

The ability of micropatterned surfaces to modulate cell behavior is combined with the well-known angiogenic property of the hyaluronan-Cu (II) complex. Hyaluronan-Cu (II) microstripes 100 and 25 mum wide on aminosilanised glass substrates were fabricated by photoimmobilization following two different methods: i.e., method I consisting in the photoimmobilization of the Hyal-Cu (II) complex; and method II based on the photoimmobilization of Hyal followed by the coordination with Cu (II). The chemistry and topography of the fabricated micropatterned samples were investigated by ATR FT-IR, atomic absorption, AFM, SEM, and ToF-SIMS. ATR FT-IR analysis demonstrated that hyaluronan conjugated with a photoreactive moiety was able to coordinate Cu (II) ions and that the photoimmobilization process was successful, as indicated by the intensity decrease of the IR band of the azidic group after the photoreaction. AFM and SEM images showed that reproducible Hyal-Cu (II) microstructures with both chemical and topographical heterogeneities have been obtained by the two preparation methods. The distribution of copper on the fabricated Hyal-Cu (II) microstructures has been investigated by ToF-SIMS. In both ToF-SIMS images and spectra, on Hyal-Cu (II) microstructures prepared by method I, the Cu peak (63 m/z) was detected only on the Hyal-Cu (II) microstripes, while on Hyal-Cu (II) microstructures prepared by method II, the Cu peak showed the same intensity both on the Hyal-Cu (II) microstripes and on the aminosilanised glass substrate, in agreement with the higher amount of Cu revealed by atomic absorption. The influence of Hyal-Cu (II) micropatterned surfaces on BAEC and LEC, in terms of migration and adhesion, has been analyzed. The results obtained indicate that Hyal-Cu (II) influences BAEC behavior inducing cell migration, while it is devoid of any effect on LEC.