Advances in Laser Additive Manufacturing of Cobalt-Chromium Alloy Multi-Layer Mesoscopic Analytical Modelling with Experimental Correlations: From Micro-Dendrite Grains to Bulk Objects.

This study presents two analytical models for the laser powder bed fusion (LPBF) process. To begin, the single layer's dimensions were measured using principal operating conditions, including laser power, laser scanning speed, powder layer thickness, and hatch distance. The single-layer printing dimensions were transformed into multi-layer printing using the hatch distance. The thermal history of the printed layers was used as an input to the Johnson-Mehl-Avrami-Kolmogorov model to estimate the average dendrite grain size. LPBF experiments were conducted for a Cobalt-chromium (Co-Cr) alloy to validate the developed model. The average dendrite grain size was estimated using a scanning electron microscope (SEM) combined with "Image J" software. The Vickers hardness test was performed to correlate the average dendrite grain size and operating conditions. A 10-15% mean absolute deviation was presented between experiments and simulation results. In all samples, a Co-based γ-FCC structure was identified. An inverse correlation was established between the laser power and smaller average dendrite grain, while a direct relationship has been determined between laser scanning speed and average dendrite grain size. A similar trend was identified between hatch distance and average dendrite grain size. A direct link has been determined between the average dendrite grain size and hardness value. Furthermore, a direct relationship has connected the laser volume energy density and hardness value. This study will help experimentalists to design operating conditions based on the required grain size and corresponding mechanical characteristics.

Influence of Silicon Carbide on Direct Powder Bed Selective Laser Process (Sintering/Melting) of Alumina.

The powder bed selective laser process (sintering/melting) has revolutionised many industries, including aerospace and biomedicine. However, PBSLP of ceramic remains a formidable challenge. Here, we present a unique slurry-based approach for fabricating high-strength ceramic components instead of traditional PBSLP. A special PBSLP platform capable of 1000 °C pre-heating was designed for this purpose. In this paper, PBSLP of Al2O3 was accomplished at different SiC loads up to 20 wt%. Several specimens on different laser powers (120 W to 225 W) were printed. When the SiC content was 10 wt% or more, the chemical interaction made it difficult to process. Severe melt pool disturbances led to poor sintering and melting. The structural analysis revealed that the micro-structure was significantly affected by the weight fraction of SiC. Interestingly, when the content was less than 2 wt%, it showed significant improvement in the microstructure during PBSLP and no effects of LPS or chemical interaction. Particularly, a crack pinning effect could be clearly seen at 0.5 wt%.

Laser Melting Deposition Additive Manufacturing of Ti6Al4V Biomedical Alloy: Mesoscopic In-Situ Flow Field Mapping via Computational Fluid Dynamics and Analytical Modelling with Empirical Testing.

Laser melting deposition (LMD) has recently gained attention from the industrial sectors due to producing near-net-shape parts and repairing worn-out components. However, LMD remained unexplored concerning the melt pool dynamics and fluid flow analysis. In this study, computational fluid dynamics (CFD) and analytical models have been developed. The concepts of the volume of fluid and discrete element modeling were used for computational fluid dynamics (CFD) simulations. Furthermore, a simplified mathematical model was devised for single-layer deposition with a laser beam attenuation ratio inherent to the LMD process. Both models were validated with the experimental results of Ti6Al4V alloy single track depositions on Ti6Al4V substrate. A close correlation has been found between experiments and modelling with a few deviations. In addition, a mechanism for tracking the melt flow and involved forces was devised. It was simulated that the LMD involves conduction-mode melt flow only due to the coaxial addition of powder particles. In front of the laser beam, the melt pool showed a clockwise vortex, while at the back of the laser spot location, it adopted an anti-clockwise vortex. During printing, a few partially melted particles tried to enter into the molten pool, causing splashing within the melt material. The melting regime, mushy area (solid + liquid mixture) and solidified region were determined after layer deposition. This research gives an in-depth insight into the melt flow dynamics in the context of LMD printing.

Keyhole Formation by Laser Drilling in Laser Powder Bed Fusion of Ti6Al4V Biomedical Alloy: Mesoscopic Computational Fluid Dynamics Simulation versus Mathematical Modelling Using Empirical Validation.

In the laser powder bed fusion (LPBF) process, the operating conditions are essential in determining laser-induced keyhole regimes based on the thermal distribution. These regimes, classified into shallow and deep keyholes, control the probability and defects formation intensity in the LPBF process. To study and control the keyhole in the LPBF process, mathematical and computational fluid dynamics (CFD) models are presented. For CFD, the volume of fluid method with the discrete element modeling technique was used, while a mathematical model was developed by including the laser beam absorption by the powder bed voids and surface. The dynamic melt pool behavior is explored in detail. Quantitative comparisons are made among experimental, CFD simulation and analytical computing results leading to a good correspondence. In LPBF, the temperature around the laser irradiation zone rises rapidly compared to the surroundings in the powder layer due to the high thermal resistance and the air between the powder particles, resulting in a slow travel of laser transverse heat waves. In LPBF, the keyhole can be classified into shallow and deep keyhole mode, controlled by the energy density. Increasing the energy density, the shallow keyhole mode transforms into the deep keyhole mode. The energy density in a deep keyhole is higher due to the multiple reflections and concentrations of secondary reflected beams within the keyhole, causing the material to vaporize quickly. Due to an elevated temperature distribution in deep keyhole mode, the probability of pores forming is much higher than in a shallow keyhole as the liquid material is close to the vaporization temperature. When the temperature increases rapidly, the material density drops quickly, thus, raising the fluid volume due to the specific heat and fusion latent heat. In return, this lowers the surface tension and affects the melt pool uniformity.

Laser Powder Bed Fusion (LPBF) of In718 and the Impact of Pre-Heating at 500 and 1000 °C: Operando Study.

The morphology of a melt pool has a critical role in laser powder bed fusion (LPBF). Nevertheless, directly characterizing the melt pool during LPBF is incredibly hard. Here, we present the melt pool flow of the entire melt pool in 3D using mesoscopic simulation models. The physical processes occurring within the melt pool are pinpointed. The flow patterns throughout the same are exposed and measured. Moreover, the impact of pre-heating at 500 and 1000 °C has been described. The study findings offer insights into LPBF. The findings presented here are critical for comprehending the LPBF and directing the establishment of improved metrics for process parameters optimization.

Full-Field Mapping and Flow Quantification of Melt Pool Dynamics in Laser Powder Bed Fusion of SS316L.

Laser powder bed fusion (LPBF) has a wide range of uses in high-tech industries, including the aerospace and biomedical fields. For LPBF, the flow of molten metal is crucial; until now, however, the flow in the melt pool has not been described thoroughly in 3D. Here, we provide full-field mapping and flow measurement of melt pool dynamics in laser powder bed fusion, through a high-fidelity numerical model using the finite volume method. The influence of Marangoni flow, evaporation, as well as recoil pressure have been included in the model. Single-track experiments were conducted for validation. The temperature profiles at different power and speed parameters were simulated, and results were compared with experimental temperature recordings. The flow dynamics in a single track were exposed. The numerical and experimental findings revealed that even in the same melting track, the melt pool's height and width can vary due to the strong Marangoni force. The model showed that the variation in density and volume for the same melting track was one of the critical reasons for defects. The acquired findings shed important light on laser additive manufacturing processes and pave the way for the development of robust, computational models with a high degree of reliability.