Water-insoluble fibres, threads, and fabrics from lauroyl derivatives of hyaluronan.

Hyaluronan (HA) is a naturally occurring polysaccharide widely used in medicine and cosmetics. To further broaden its potential, various HA derivatives have been developed with the aim of reducing solubility, slowing degradation, or providing other beneficial properties. However, for most medical applications, these derivatives must be processed into suitable forms. Here we present water-insoluble fibres prepared from lauroyl-modified HA using a wet spinning process. Important properties of the fibres, such as swelling or the degradation rate, can be fine-tuned by adjusting the degree of HA modification. Due to their mechanical properties, the lauroyl HA fibres can be easily processed into threads and subsequently into fabrics of various sizes, shapes, and degrees of porosity. In addition, in vitro cytotoxicity testing of the fibres showed that they were non-cytotoxic. Overall, our results suggest that lauroyl HA fibres are a promising material that could be used to develop a variety of medical devices.

Fabrication of biodegradable textile scaffold based on hydrophobized hyaluronic acid.

In this work, we report on the preparation of a novel biodegradable textile scaffold made of palmitoyl-hyaluronan (palHA). Monofilament fibres of palHA with a diameter of 120µm were prepared by wet spinning. The wet-spun fibres were subsequently processed into a warp-knitted textile. To find a compromise between swelling in water and degradability of the final textile scaffold, a series of palHA derivatives with different degrees of substitution of the palmitoyl chain was synthesized. Freeze-drying not only provided shape fixation, but also speeded up scaffold degradation in vitro. Fibronectin, fibrinogen, laminin and collagen IV were physically adsorbed on the textile surface to enhance cell adhesion on the material. The highest amount of adsorbed cell-adhesive proteins was achieved with fibronectin (89%), followed by fibrinogen (81%). Finally, textiles modified with fibronectin or fibrinogen both supported the adhesion and proliferation of normal human fibroblasts in vitro, proving to be a useful cellular scaffold for tissue engineering.