Microstructural, mechanical and corrosion characteristics of heat-treated Mg-1.2Zn-0.5Ca (wt%) alloy for use as resorbable bone fixation material.

Mg-Zn-Ca alloys have grabbed most of the recent attention in research attempting to develop an Mg alloy for bone fixation devices due to their superior biocompatibility. However, early resorption and insufficient strength remain the main problems that hinder their use. Heat treatment has previously been thoroughly studied as a post-shaping process, especially after the fabrication of complex parts (e.g. porous structures) by 3D-printing or powder metallurgy. In this work, the effect of heat treatment on Mg-1.2Zn-0.5Ca (wt%) alloy's microstructural, mechanical and corrosion properties was studied. The surface morphology of samples was characterized by optical microscopy, scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), and x-ray diffraction (XRD). Hardness, compression and tensile tests were conducted, while the in vitro corrosion characteristics of the prepared samples were determined using potentiodynamic polarization (PDP) and immersion tests. It was found that increasing the age hardening duration up to 2-5h increased the heat-treated Mg-1.2Zn-0.5Ca alloy's mechanical properties. Further increase in the age hardening duration did not result in further enhancement in mechanical properties. Similarly, heat treatment significantly altered the Mg-1.2Zn-0.5Ca alloy's in vitro corrosion properties. The corrosion rate of the Mg-1.2Zn-0.5Ca alloy after the heat treatment process was reduced to half of that for the as-cast alloy. XRD results showed the formation of biocompatible agglomerations of hydroxyapatite (HA) and magnesium hydroxide (Mg(OH)2) on the corroded surface of the heat-treated Mg-1.2Zn-0.5Ca alloy samples. The performed heat treatment process had a significant effect on both mechanical and corrosion properties of the prepared Mg-1.2Zn-0.5Ca alloy. The age hardening duration which caused the greatest increase in mechanical and the most slowed corrosion rate for Mg-1.2Zn-0.5Ca alloy material was between 2 and 5h.

Resorbable bone fixation alloys, forming, and post-fabrication treatments.

Metallic alloys have been introduced as biodegradable metals for various biomedical applications over the last decade owing to their gradual corrosion in the body, biocompatibility and superior strength compared to biodegradable polymers. Mg alloys possess advantageous properties that make them the most extensively studied biodegradable metallic material for orthopedic applications such as their low density, modulus of elasticity, close to that of the bone, and resorbability. Early resorption (i.e., <3months) and relatively inadequate strength are the main challenges that hinder the use of Mg alloys for bone fixation applications. The development of resorbable Mg-based bone fixation hardware with superior mechanical and corrosion performance requires a thorough understanding of the physical and mechanical properties of Mg alloys. This paper discusses the characteristics of successful Mg-based skeletal fixation hardware and the possible ways to improve its properties using different methods such as mechanical and heat treatment processes. We also review the most recent work pertaining to Mg alloys and surface coatings. To this end, this paper covers (i) the properties and development of Mg alloys and coatings with an emphasis on the Mg-Zn-Ca-based alloys; (ii) Mg alloys fabrication techniques; and (iii) strategies towards achieving Mg-based, resorbable, skeletal fixation devices.