Functional Materials for Fabrication of Carbon-Based Perovskite Solar Cells: Ink Formulation and Its Effect on Solar Cell Performance.

Perovskite solar cells (PSCs) have rapidly developed into one of the most attractive photovoltaic technologies, exceeding power conversion efficiencies of 25% and as the most promising technology to complement silicon-based solar cells. Among different types of PSCs, carbon-based, hole-conductor-free PSCs (C-PSCs), in particular, are seen as a viable candidate for commercialization due to the high stability, ease of fabrication, and low cost. This review examines strategies to increase charge separation, extraction, and transport properties in C-PSCs to improve the power conversion efficiency. These strategies include the use of new or modified electron transport materials, hole transport layers, and carbon electrodes. Additionally, the working principles of various printing techniques for the fabrication of C-PSCs are presented, as well as the most remarkable results obtained from each technique for small-scale devices. Finally, the manufacture of perovskite solar modules using scalable deposition techniques is discussed.

Influence of Redox Couple on the Performance of ZnO Dye Solar Cells and Minimodules with Benzothiadiazole-Based Photosensitizers.

ZnO-based dye-sensitized solar cells exhibit lower efficiencies than TiO2-based systems despite advantageous charge transport dynamics and versatility in terms of synthesis methods, which can be primarily ascribed to compatibility issues of ZnO with the dyes and the redox couples originally optimized for TiO2. We evaluate the performance of solar cells based on ZnO nanomaterial prepared by microwave-assisted solvothermal synthesis, using three fully organic benzothiadiazole-based dyes YKP-88, YKP-137, and MG-207, and alternative electrolyte solutions with the I-/I3 -, Co(bpy)3 2+/3+, and Cu(dmp)2 1+/2+ redox couples. The best cell performance is achieved for the dye-redox couple combination YKP-88 and Co(bpy)3 2+/3+, reaching an average efficiency of 4.7% and 5.0% for the best cell, compared to 3.7% and 3.9% for the I-/I3 - couple with the same dye. Electrical impedance spectroscopy highlights the influence of dye and redox couple chemistry on the balance of recombination and regeneration kinetics. Combined with the effects of the interaction of the redox couple with the ZnO surface, these aspects are shown to determine the solar cell performance. Minimodules based on the best systems in both parallel and series configurations reach 1.5% efficiency for an area of 23.8 cm2.

Open-Circuit Voltage (V OC) Enhancement in TiO2-Based DSSCs: Incorporation of ZnO Nanoflowers and Au Nanoparticles.

An important reason for the relatively low efficiency of dye-sensitized solar cells (DSSCs) is the low open-circuit voltage (V OC) of about 0.7 V for a standard solar cell with a dye that has an absorption onset at 1.6 eV. We report an enhancement of the V OC of about 0.10 V with respect to a TiO2-based DSSC modified with ZnO nanoflowers that we prepared by a new and facile method. An additional increase of the V OC of about 0.08 V was achieved by modifying the ZnO nanoflowers with Au nanoparticles, resulting in a DSSC with an efficiency of 2.79%, highlighted by a high V OC of 0.89 V. Detailed analysis with electrochemical impedance spectroscopy and intensity-modulated photovoltage and photocurrent spectroscopies (IMVS and IMPS) reveal that the main reason for the increase of V OC is related to the shift of the band edges upon coupling TiO2 with ZnO nanoflowers, even though the electron lifetime at the same charge density actually decreases. These results show the intricate interplay between band edge shift, recombination kinetics, and DSSC performance and illustrate that a higher voltage DSSC can be fabricated by modification of the photoanode materials.