This paper verified the possibility of applying chitosan and/or ferulic acid or polycaprolactone (PCL)-based coatings to polydimethylsiloxane/neodymium-iron-boron (PDMS/NdFeB) composites using the spin-coating method. The surface modification of magnetic composites by biofunctional layers allows for the preparation of materials for biomedical applications. Biofunctional layered magnetic composites were obtained in three steps. The spin-coating method with various parameters (time and spin speed) was used to apply different substances to the surface of the composites. Scanning electron microscopy (SEM) and confocal laser scanning microscopy (CLSM) were used to analyze the thickness and surface topography. The contact angle of the obtained surfaces was tested. Increasing spin speed and increasing process time for the same speed resulted in decreasing the composite's thickness. The linear and surface roughness for the prepared coatings were approximately 0.2 µm and 0.01 µm, respectively, which are desirable values in the context of biocompatibility. The contact angle test results showed that both the addition of chitosan and PCL to PDMS have reduced the contact angle θ from 105° for non-coated composite to θ~59-88° depending on the coating. The performed modifications gave promising results mainly due to making the surface hydrophilic, which is a desirable feature of projected biomaterials.
RESUMO
Magnetic micro- and nanoparticles (MPs)-based composite materials are widely used in various applications in electronics, biotechnology, and medicine. This group of silicone composites have advantageous magnetic and mechanical properties as well as sufficient flexibility and biocompatibility. These composites can be applied in medicine for biological sensing, drug delivery, tissue engineering, and as remote-controlled microrobots operating in vivo. In this work, the properties of polydimethylsiloxane (PDMS)-based composites with different percentages (30 wt.%, 50 wt.%, 70 wt.%) of NdFeB microparticles as a filler were characterized. The novelty of the work was to determine the influence of the percentage of MP content and physiological conditioning on the properties of the PDMS-MP composites after in vitro incubation. An important essence of the work was a comprehensive study of the properties of materials important from the point of view of medical applications. Materials were tested before and after conditioning in 0.9 wt.% NaCl solution at a temperature of 37 °C. Several studies were carried out, including thermal, physicochemical, and rheological tests. The results show that with an increase of the incubation time, most of the measured thermal and physicochemical parameters decreased. The presence of the magnetic filler, especially at a concentration of 70 wt.%, has a positive effect on thermal stability and physicochemical and rheological properties. The performed tests provided important results, which can lead to further research for a broader application of magnetic composites in the biomedical field.