RESUMO
Tribological studies of the 2D nanoadditives such as MoS2 and graphene are mostly performed in base oils such as SN500, SN150, or paraffin. We have focused on their effect in lubrication properties of industrial oils (e.g., axle, transmission, and compressor oils) along with SN500 oil employing a four-ball tester. Two types of graphene powders (GpowA with fewer defects than GpowC), MoS2 powder, and their physical mixtures are chosen as nanoadditives. The tribology performance for 0.05 wt% of additives in various industrial oils is evaluated by monitoring the coefficient of friction (COF) during rubbing and wear scar diameter (WSD) of the steel balls after rubbing. Elemental analysis and electron microscopy have been performed on the wear surfaces for evidence of any tribofilm formation. GpowA favors antifriction for axle and transmission oils with 40% reduction in axle oil, whereas it improved antiwear properties in most of the oils. GpowC shows a COF decrement by 12% only for compressor oil, but contribute to wear reduction in all oils. The observed COF reduction is attributed to the compatibility of nonfunctionalized GpowA with nonpolar axle oil and functionalized GpowC with polar compressor oil. MoS2 shows a decrease in the COF and WSD in most industrial oils; the best being 60% COF and 7% WSD reduction in axle oil. For additives in oils that favor antiwear, flakes or particles are observed on the wear surface supported by the higher elemental contribution of the constituents from the wear region. The mixtures of GpowA or C with MoS2, however, does not seem to favor improvement in the COF or WSD in industrial oils. With assistance from oleylamine surfactants, the lubrication properties of most additives are improved, particularly for the mixtures with 12-15% COF reduction and 4-7% WSD reduction in compressor oil. The study indicates that a large sheet size of high-quality graphene aids antifriction and addition of surfactant molecules facilitates a co-operative effect between MoS2 and graphene for improved tribology.
RESUMO
Enhancing the surface-enhanced Raman scattering (SERS) activity of semiconductor metal oxide nanostructures by controlling the morphology and oxygen vacancies towards trace detection of organics is of significant interest. In this study, MoO3 with a novel sea urchin morphology is synthesized employing chemical bath deposition and consists of hundreds of â¼15 µm long spikes originating from the core forming 20-40 micron globular structures. The spikes taper to form 20 nm sharp tips. SERS of rhodamine 6G (R6G) over MoO3 sea urchins has been investigated and compared to that of 1D h-MoO3 nanorod arrays. The SERS activity is morphology dependent and the sea urchin-like morphology exhibits higher SERS activity with an enhancement factor (EF) of the order 105 and a detection limit of 100 nM, while for h-MoO3 nanorods, the corresponding values are 103 and 1 µM, respectively. X-ray photoelectron spectroscopy reveals a high concentration of Mo+5 states in sea urchins indicating lattice oxygen vacancies. The observed EF is quite high for a metal oxide substrate and is attributed to the enhanced charge transfer between analyte molecules and the substrate promoted by the oxygen vacancies along with surface defects and hydroxyl groups on MoO3 sea urchins providing more active sites for the adsorption of probe molecules. The role of oxygen vacancies is confirmed by the lower EF value exhibited by the stoichiometric 1D h-MoO3. Raman mapping of a single sea urchin is achieved with good R6G intensity and indicates that the tips of spiky features are involved in SERS enhancement. The reusability of substrates is shown for repeated cycles of R6G adsorption by UV irradiation exploiting the photocatalytic activity of MoO3 nanostructures.
