Efficient anti-corrosive coating of cold-rolled steel in a seawater environment using an oil-based graphene oxide ink.

We report the production of an efficient anti-corrosive coating of cold-rolled (CR) steel in a seawater environment (∼3.5 wt% NaCl aqueous solution) using an oil-based graphene oxide ink. The graphene oxide was produced by heating Aeschynomene aspera plant as a carbon source at 1600 °C in an argon atmosphere. The ink was prepared by cup-milling the mixture of graphene oxide and sunflower oil for 10 min. The coating of ink on the CR steel was made using the dip-coating method, followed by curing at 350 °C for 10 min in air atmosphere. The results of the potentiodynamic polarization show that the corrosion rate of bare CR steel decreases nearly 10,000-fold by the ink coating. Furthermore, the salt spray test results show that the red rusting in the ink-coated CR steel is initiated after 100 h, in contrast to 24 h and 6 h in the case of oil-coated and bare CR steel, respectively. The significant decrease in the corrosion rate by the ink-coating is discussed based on the impermeability of graphene oxide to the corrosive ions.

Near-grain-boundary characterization by atomic force microscopy.

Characterization of near-grain boundary is carried out by atomic force microscopy (AFM). It has been observed to be the most suitable technique owing to its capability to investigate the surface at high resolution. Commercial purity-grade nickel processed under different conditions, viz., (i) cold-rolled and annealed and (ii) thermally etched condition without cold rolling, is considered in the present study. AFM crystallographic data match well with the standard data. Hence, it establishes two grain-boundary relations viz., plane matching and coincidence site lattice (CSL Sigma=9) relation for the two different sample conditions.