Composition templating for heterogeneous nucleation of intermetallic compounds.

Refinement of intermetallic compounds (IMCs) through enhancing heterogeneous nucleation during casting process is an important approach to improve the properties of aluminium alloys, which greatly increases the economy value of recycled Al-alloys. However, heterogeneous nucleation of IMCs is inherently more difficult than that of a pure metal or a solid solution. It requires not only creation of a crystal structure but also the positioning of 2 or more different types of atoms in the lattice with specific composition close to that of the nucleated IMCs. Previous understanding on heterogeneous nucleation is based on structural templating, usually considering the small lattice misfit at the interface between the nucleating solid and substrate. In this work, we proposed a hypothesis and demonstrated that composition templating plays a critical role in heterogeneous nucleation of IMCs. The experimental results revealed that segregation of Fe atoms on the AlB2 surface, i.e., the Fe modified AlB2 particle, provides the required composition templating and hence enhances heterogeneous nucleation of α-Al15(Fe, Mn)3Si2, resulting in a significant refinement of the α-Al15(Fe, Mn)3Si2 particles in an Al-5 Mg-2Si-1.0Mn-1.2Fe alloy.

Impeding Nucleation for More Significant Grain Refinement.

Grain refinement has been a topic of extensive research due to its scientific and technological importance as a common industrial practice for over seven decades. The traditional approach to grain refinement has been to reduce nucleation undercooling by the addition of potent nucleant particles. Here we show both theoretically and experimentally that more significant grain refinement can be achieved through increasing nucleation undercooling by using impotent nucleant particles. Based on the concept of explosive grain initiation, this new approach is illustrated by grain initiation maps and grain refinement maps and validated by experiments. It is anticipated that this new approach may lead to a profound change in both nucleation research and industrial practice well beyond metal casting.