Biocompatibility, bioactive potential, porosity, and interface analysis calcium silicate repair cements in a dentin tube model.

OBJECTIVES: This study is to evaluate biocompatibility, bioactive potential, porosity, and dentin/material interface of Bio-C Repair (BIOC-R), MTA Repair HP (MTAHP), and Intermediate Restorative Material (IRM). MATERIALS AND METHODS: Dentin tubes were implanted into subcutaneous of rats for 7, 15, 30, and 60 days. Thickness of capsules, number of inflammatory cells (ICs), interleukin-6 (IL-6), osteocalcin (OCN), and von Kossa were evaluated. Porosity and material/dentin interface voids were also analyzed. Data were submitted to ANOVA and Tukey's tests (p < 0.05). RESULTS: IRM capsules were thicker and contained greater ICs and IL-6-immunopositive cells at 7 and 15 days. BIOC-R capsules exhibited higher thickness and ICs at 7 days and greater IL-6 at 7 and 15 days than MTAHP (p < 0.05). At 30 and 60 days, no significant difference was observed among the groups. OCN-immunopositive cells, von Kossa-positive, and birefringent structures were observed in BIOC-R and MTAHP. MTAHP exhibited higher porosity and interface voids (p < 0.05). CONCLUSIONS: BIOC-R, MTAHP, and IRM are biocompatible. Bioceramics materials demonstrate bioactive potential. MTAHP presented the highest porosity and presence of voids. CLINICAL RELEVANCE: BIOC-R and MTAHP have adequate biological properties. BIOC-R demonstrated lower porosity and presence of voids, which may represent better sealing for its clinical applications.

Biocompatibility and bioactive potential of an experimental tricalcium silicate-based cement in comparison with Bio-C repair and MTA Repair HP materials.

AIM: To evaluate the tissue reaction of a tricalcium silicate-based repair material associated with 30% calcium tungstate (TCS + CaWO4 ) in comparison to Bio-C Repair (Bio-C; Angelus) and to MTA Repair HP (MTA HP; Angelus). METHODOLOGY: Polyethylene tubes filled with one of the materials or left empty (control group, CG) were implanted into the subcutaneous tissues of rats for 7, 15, 30 and 60 days (n = 32/group). The capsule thickness, number of inflammatory cells, collagen content, interleukin-6 (IL-6), osteocalcin (OCN), von Kossa reaction and analysis under polarized light were evaluated. The data were subjected to generalized linear models for repeated measures, except the OCN. OCN data were submitted to Kruskal-Wallis and Dunn's post hoc test and Friedman followed by Nemenyi's test at significance level of 5%. RESULTS: At all time points, significant differences in the number of inflammatory cells were not observed between TCS + CaWO4 and Bio-C, whereas, at 15, 30 and 60 days, no significant difference was detected between TCS + CaWO4 and MTA HP. At all periods, significant differences were not detected in the number of fibroblasts in TCS + CaWO4 versus MTA HP, and, at 60 days, no significant difference was demonstrated between these groups and CG. Significant differences in the immunoexpression of IL-6 were not detected amongst bioceramic materials at all periods. From 7 to 60 days, significant reduction in the number of inflammatory cells, number of IL-6-immunopositive cells and in the capsule thickness was accompanied by significant increase in the collagen in all groups. OCN-immunolabelled cells, von Kossa-positive structures and amorphous calcite deposits were observed around all materials, whereas, in the CG, these structures were not seen. CONCLUSIONS: These findings indicate that the experimental material (TCS + CaWO4 ) is biocompatible and has a bioactive potential, similar to the MTA HP and Bio-C Repair, and suggest its use as a root repair material.

Bioactive potential of Bio-C Pulpo is evidenced by presence of birefringent calcite and osteocalcin immunoexpression in the rat subcutaneous tissue.

As the biocompatibility and bioactive potential of repair materials are desired characteristics in dentistry, the tissue response of Bio-C Pulpo, a bioceramic material launched on the marked by Angelus (Brazil), was compared with Biodentine (Septodont, France) and White MTA (WMTA; Angelus, Brazil). In 32 rats, 148 polyethylene tubes filled with Bio-C Pulpo, Biodentine or WMTA, and empty (CG, control group) were implanted into subcutaneous tissues for 7, 15, 30, and 60 days. The capsule thickness, numerical density of inflammatory cells (IC) and fibroblasts (Fb), amount of collagen, immunohistochemistry detection of interleukin-6 (IL-6) and osteocalcin (OCN), von Kossa and analysis under polarized light were performed. Data were subjected to two-way ANOVA followed by Tukey's test (p ≤ 0.05). At 7 and 15 days, the capsules around Bio-C Pulpo were thicker than in WMTA while, at 30 and 60 days, significant differences were not observed among the groups. Although at 7, 15, and 30 days, a greater number of IL-6-immunostained cells was found in Bio-C Pulpo and Biodentine than in WMTA, no significant difference was detected among the groups at 60 days. In all groups, the number of Fb and collagen content increased significantly over time. The capsules around materials exhibited von Kossa-positive and birefringent structures, and OCN-immunostained cells whereas, in the CG, these structures were not observed. Bio-C Pulpo, similarly to Biodentine and WMTA, is biocompatible, allows the connective tissue repair and presents bioactive potential in connective tissue of rats.

Physicochemical, biological, and antibacterial evaluation of tricalcium silicate-based reparative cements with different radiopacifiers.

OBJECTIVE: To evaluate tricalcium silicate-based (TCS) experimental materials, associated with zirconium oxide (ZrO2), calcium tungstate (CaWO4) or niobium oxide (Nb2O5) radiopacifiers, in comparison with MTA Repair HP (Angelus). METHODS: Physicochemical tests: setting time, radiopacity, pH and solubility. In vitro assays: cytotoxicity: MTT and Neutral Red - NR; cell bioactivity: alkaline phosphatase activity (ALP), Alzarin red staining (ARS) and real time PCR (qPCR). Antibacterial activity: direct contact on Enterococcus faecalis in the planktonic form. Physicochemical and ARS data were submitted to ANOVA/Tukey tests; antibacterial activity, to Kruskall-Wallis and Dunn tests; MTT, NR, ALP and qPCR were analyzed by ANOVA/Bonferroni tests (α = 0.05). RESULTS: TCS + CaWO4 presented the longest setting time and MTA HP the shortest. Except for TCS, all the materials presented radiopacity above 3 mmAl. The cements had alkaline pH, antibacterial activity, low solubility and no cytotoxic effects. The highest ALP activity occurred in 14 days, especially to TCS, TCS + ZrO2 and TCS + CaWO4. TCS + ZrO2, TCS + Nb2O5 and MTAHP had higher mineralized nodule formation than those of the negative control (NC). After 7 days, there was no difference in mRNA expression for ALP, when compared to NC. However, after 14 days there was no overexpressed ALP mRNA, especially TCS + Nb2O5, in relation to the CN. All the materials presented antimicrobial action. SIGNIFICANCE: The pure tricalcium silicate associated with ZrO2, CaWO4 or Nb2O5 had appropriate physicochemical properties, antibacterial activity, cytocompatibility and induced mineralization in Saos-2, indicating their use as reparative materials.