This article focuses on the surface reactivity of two spinel samples with different stoichiometries and crystal morphologies, namely Li1+xMn2-xO4 with x = 0.05 and 0.10. LiMn2O4 compounds are good candidates as positive electrode of high-power lithium-ion batteries for portable devices. The samples were investigated using both experimental and theoretical approaches. On the experimental point of view, they were characterized in depth from X-ray diffraction, scanning electron microscopy, and X-ray photoelectron spectroscopy (XPS) analyses. Then, the reactivity was investigated through the adsorption of (SO2) gaseous probes, in controlled conditions, followed by XPS characterization. First-principle calculations were conducted simultaneously to investigate the electronic properties and the reactivity of relevant surfaces of an ideal LiMn2O4 material. The results allow us to conclude that the reactivity of the samples is dominated by an acido-basic reactivity and the formation of sulfite species. Nonetheless, on the x = 0.05 sample, both sulfite and sulfate species are obtained, the later, in lesser extent, corresponding to a redox reactivity. Combining experimental and theoretical results, this redox reactivity could be associated with the presence of a larger quantity of Mn4+ cations on the last surface layers of the material linked to a specific surface orientation.
RESUMO
This article deals with the surface reactivity of (001)-oriented Li2MnO3 crystals investigated from a multitechnique approach combining material synthesis, X-ray photoemission spectroscopy (XPS), scanning electron microscopy, Auger electron spectroscopy, and first-principles calculations. Li2MnO3 is considered as a model compound suitable to go further in the understanding of the role of tetravalent manganese atoms in the surface reactivity of layered lithium oxides. The knowledge of the surface properties of such materials is essential to understand the mechanisms involved in parasitic phenomena responsible for early aging or poor storage performances of lithium-ion batteries. The surface reactivity was probed through the adsorption of SO2 gas molecules on large Li2MnO3 crystals to be able to focus the XPS beam on the top of the (001) surface. A chemical mapping and XPS characterization of the material before and after SO2 adsorption show in particular that the adsorption is homogeneous at the micro- and nanoscale and involves Mn reduction, whereas first-principles calculations on a slab model of the surface allow us to conclude that the most energetically favorable species formed is a sulfate with charge transfer implying reduction of Mn.