The behavior of thermally modified wood after exposure in maritime/industrial and urban environments.

Natural and thermally modified Pine, Ash, and Acacia woods were exposed in two different environments: urban and maritime/industrial. The weathering effects were evaluated during 24 months regarding color, chemical, and structural changes. In all wood species, thermal modification induced color, chemical, and structural changes. All woods became darker (Pine ΔL*: -32.01; Ash ΔL*: -36.83; Acacia ΔL*: -27.50), total extractives content increased (Pine: 19 %; Ash: 32 % and Acacia: 18 %), and the samples presented deformation and damaged cells. Total lignin was not significantly changed, although there were detected changes in lignin, namely the reduction of G-units in Pine (≈2 %) and reduction of S/G ratio in Acacia (≈0.04 %). Ash remained almost the same. After weathering, modified woods suffered fewer color changes, indicating that the thermal modification could improve the resistance to color change. Acacia wood, when exposed to maritime/industrial conditions, revealed a higher color change (ΔE: 35.7 at 24 months) when compared with urban conditions (ΔE: 23.5 at 24 months). Delignification, possibly caused by photodegradation, occurred in all wood samples, and the loss of extractive happened, perhaps caused by rain. Modified woods were slightly less resistant to weathering in maritime/industrial environments. Some structural damage, namely cracked cells, the appearance of molds, blue staining, and particle deposition, was observed. The thermal modification enables color stabilization but does not seem to improve the weathering resistance in all studied wood species. Exposure to the different environments did not lead to significant differences in the morphology and chemical composition of the three natural and modified wood species.

Bark anatomy, chemical composition and ethanol-water extract composition of Anadenanthera peregrina and Anadenanthera colubrina.

The bark of Anadenanthera peregrina (L.) Speg and Anadenanthera colubrina (Vell.) Brenan were characterized in relation to anatomical and chemical features. The barks were similar and included a thin conducting phloem, a largely dilated and sclerified non-conducting phloem, and a rhyridome with periderms with thin phellem interspersed by cortical tissues. Only small differences between species were observed that cannot be used alone for taxonomic purposes. The summative chemical composition of A. peregrina and A. colubrina was respectively: 8.2% and 7.7% ash; 28.8% and 29.3% extractives; 2.4% and 2.6% suberin; and 18.9% lignin. The monosaccharide composition showed the predominance of glucose (on average 82% of total neutral sugars) and of xylose (9%). The ethanol-water extracts of A. peregrina and A. colubrina barks included a high content of phenolics, respectively: total phenolics 583 and 682 mg GAE/g extract; 148 and 445 mg CE/g extract; tannins 587 and 98 mg CE/g extract. The antioxidant activity was 238 and 269 mg Trolox/g extract. The barks of the Anadenanthera species are a potential source of polar extractives that will represent an important valorization and therefore contribute to improve the overall economic potential and sustainability of A. peregrina and A. colubrina.

Growth rate and ring width variability of teak, Tectona grandis (Verbenaceae) in an unmanaged forest in East Timor.

Teak (Tectona grandis) is one of the most valuable timbers in international trade and an important species for tropical forestry. Teak is found on the island of East Timor but no information is available on teak growth from this region. A pure stand planted in 1940-50 in the North of East Timor and left unmanaged was studied. Fifteen trees were sampled in October-November 2003 and stem discs taken at three height levels of its height (1.7m, 9.5m and 18.7m), and cores were collected at DBH. Transverse surfaces of the discs and cores were polished for ring identification. Core cross sections were first digitized and disc cross sections were observed under the microscope. Three randomly selected radii were analyzed in each disc. Ring width measurement and ring counting were done using image analysis software. The distinction between heartwood and sapwood was performed macroscopically by colour difference, and heartwood radius and sapwood width were measured. The relationship between stem and heartwood radius was studied for each disc and heartwood percentage by radius was determined. Radial ring width curves are presented for the different axial positions within the stem, and ring width variability was analyzed. Growth rates were calculated and age-radius relationships were estimated using cumulative growth curves. Growth rings were large and well defined in the juvenile phase, reflecting the specie's fast-growing character. The year-to-year variation of ring width showed a similar pattern among trees. Mean ring width ranged between 4.3-7.3mm for the first 20 years and 3.3-5.1mm for 30 to 45 years. Pith eccentricity was evident in the lower part of the stem and ring wedging occurred. On average, heartwood represented 84% of the radius and sapwood contained 6 to 11 rings. The age-related variation of ring width and the occurrence in the lower part of the tree stems of eccentricity and wedging rings, highlights the importance of appropriate stand management, particularly regarding basal density distribution over time, whenever optimized timber production is envisaged.

Growth rate and ring width variability of teak, Tectona grandis (Verbenaceae) in an unmanaged forest in East Timor

Teak (Tectona grandis) is one of the most valuable timbers in international trade and an important species for tropical forestry. Teak is found on the island of East Timor but no information is available on teak growth from this region. A pure stand planted in 1940-50 in the North of East Timor and left unmanaged was studied. Fifteen trees were sampled in October-November 2003 and stem discs taken at three height levels of its height (1.7m, 9.5m and 18.7m), and cores were collected at DBH. Transverse surfaces of the discs and cores were polished for ring identification. Core cross sections were first digitized and disc cross sections were observed under the microscope. Three randomly selected radii were analyzed in each disc. Ring width measurement and ring counting were done using image analysis software. The distinction between heartwood and sapwood was performed macroscopically by colour difference, and heartwood radius and sapwood width were measured. The relationship between stem and heartwood radius was studied for each disc and heartwood percentage by radius was determined. Radial ring width curves are presented for the different axial positions within the stem, and ring width variability was analyzed. Growth rates were calculated and age-radius relationships were estimated using cumulative growth curves. Growth rings were large and well defined in the juvenile phase, reflecting the specie’s fast-growing character. The year-to-year variation of ring width showed a similar pattern among trees. Mean ring width ranged between 4.3-7.3mm for the first 20 years and 3.3-5.1mm for 30 to 45 years. Pith eccentricity was evident in the lower part of the stem and ring wedging occurred. On average, heartwood represented 84% of the radius and sapwood contained 6 to 11 rings. The age-related variation of ring width and the occurrence in the lower part of the tree stems of eccentricity and wedging rings, highlights the importance of appropriate stand management, particularly regarding basal density distribution over time, whenever optimized timber production is envisaged.

La madera de teca (Tectona grandis L.f.) es una de las más valiosas en el comercio internacional y una especie importante para la silvicultura tropical. La teca se encuentra en la isla de Timor Leste, pero no existe información disponible sobre su crecimiento en esta región. Se estudió una plantación pura no manejada que fue establecida entre 1940 y 1950 en el Norte de Timor Leste. Entre Octubre- Noviembre 2003 se cosecharon 15 árboles y al tronco se les extrajeron discos a tres niveles de altura (1.7m, 9.5m y 18.7 m), y se recolectaron núcleos a la altura del pecho (DAP). El conteo y la medición de los anillos se realizaron mediante el software de análisis de imagen. La distinción entre el duramen y la albura se realizó macroscópicamente por la diferencia de color, y se midieron el radio del duramen y el ancho de la albura. Para cada disco se estudió la relación entre el tallo y radio del duramen y el porcentaje del duramen. Las curvas de variación del ancho de los anillos se presentan para las diferentes posiciones axiales dentro del tronco y se analizó la variabilidad del ancho de los anillos. Las tasas de crecimiento fueron calculadas y las relaciones de radio con la edad se calcularon usando las curvas de crecimiento acumulado. Los anillos de crecimiento eran grandes y bien definidos en la fase juvenil, lo que refleja el carácter de crecimiento rápido de esta especie. La variación en la anchura de los anillos año a año mostró un patrón similar entre los árboles. La anchura media del anillo osciló entre 4.3-7.3mm para los primeros 20 años y 3.3-5.1mm para los de 30 a 45 años. La excentricidad de la médula fue evidente en la parte inferior del tallo y se observó la formación de anillos sobrepuestos. En promedio, el duramen representó el 84% del radio y la albura mostró entre 6 y 11 anillos. La variación del ancho de los anillos con la edad, la presencia de excentricidad en la parte inferior del árbol y los anillos sobrepuestos pone de relieve la importancia del manejo forestal con particular atención a la distribución de densidad basal en el tiempo, cuando se pretende la producción optimizada de la madera.