Low Concentrations of Gold Nanoparticles as Electric Charge Carriers in Piezoelectric Cement-Based Materials.

Piezoelectric cement-based composites could serve to monitor the strain state of structural elements or act as self-powered materials in structural health monitoring (SHM) applications. The incorporation of piezoelectric materials as an active phase within cement matrices has presented a highly attractive avenue until today. However, their application is challenged by the low electrical conductivity of the hydrated cement matrix. Gold nanoparticles (Au NPs) possess substantial potential for elevating the free electrical charge within the matrix, increasing its electrical conductivity between the Au NPs and the cement matrix, thereby enhancing the piezoelectric response of the composite. In this sense, the objective of this study is to investigate the effects of incorporating low concentrations of gold nanoparticles (Au NPs) (442 and 658 ppm) on the electrical and piezoelectric properties of cement-based composites. Additionally, this study considers the effects of such properties when the material is cured under a constant electric field. Electrical impedance spectroscopy was used to evaluate the polarization resistance and piezoresistive properties of the material. Additionally, open-circuit potential measurements were taken alongside the application of mechanical loads to assess the piezoelectric activity of the composites. The findings revealed a notable decrease in the composite's total electrical resistance, reaching a value of 1.5 ± 0.2 kΩ, almost four times lower than the reference specimens. In the realm of piezoelectricity, the piezoelectric voltage parameter g33 exhibited a remarkable advancement, improving by a factor of 57 when compared to reference specimens. This significant enhancement can be attributed to both the concentration of Au NPs and the electrical curing process. In summary, the outcomes of this study underscore the feasibility of creating a highly electrically conductive cement-based matrix, using low concentrations of gold nanoparticles as electric charge carries, and indicate the possible piezoelectric behavior of the studied compposite.

Method for fabricating self-powered cement sensors based on gold nanoparticles.

Nowadays, cement industry researchers are working hard to develop cement sensors based on nanocomposites because they can be used to develop intelligent and sustainable civil structures, self-powered, self-healing, or self-monitoring. In this light, this paper shows a methodology to obtain piezoelectric cement sensors, which produce enough energy not to require an external power source in sensing-strain applications. Mainly, two proposed experimental procedures increased the piezoelectric properties of these cement-based composites: add gold nanoparticles in the proper concentrations and apply a constant electric field during the curing stage. Firstly, the gold nanoparticles were obtained through a pulsed laser ablation system, and their particle size distribution was measured with a particle analyzer Litesizer 500 from Anton Paar, and their morphology was corroborated using a scanning electron microscope. Two concentrations (442 ppm and 658 ppm) of gold nanoparticles were obtained by changing the total ablation time. Next, we fabricated the cement sensors as described by ASTM standards C39-C39M. Hence, the cement was hand mixed with a water-to-cement ratio (w/c) of 0.47 for then poured on cylindrical molds saving the proportions recommended by the ASTM standard; in this stage, the gold nanoparticles were already part of the water ratio. Then, the cement sensors were cured under an external electric field and dried for 24 hours more in an oven to be finally ready for electromechanical characterization. Meanwhile, the electric response in altern current and the piezoelectric behavior were corroborated through electrical impedance spectroscopy and open circuit potential measurements, respectively. The piezoelectric behavior was obtained when a compressive strength was applied to the sensor, and the generated voltage was simultaneously measured. Finally, the electrical and mechanical characterization measurements were processed and analyzed using Python scripts.•The particle size and the families amount of Au NPs are affected by the ablation time.•The correct proportion of Au NPs increases the inherent piezoelectricity of cement paste.•The piezoelectric response can be addressed by coupling electric and mechanical tests.

Time-Stability Dispersion of MWCNTs for the Improvement of Mechanical Properties of Portland Cement Specimens.

This study shows the energy optimization and stabilization in the time of solutions composed of H2O + TX-100 + Multi-Wall Carbon Nanotubes (MWCNTs), used to improve the mechanical properties of Portland cement pastes. For developing this research, sonication energies at 90, 190, 290, 340, 390, 440, 490 and 590 J/g are applied to a colloidal substance (MWCNTs/TX-100 + H2O) with a molarity of 10 mM. Raman spectroscopy analyses showed that, for energies greater than 440 J/g, there are ruptures and fragmentation of the MWCNTs; meanwhile at energies below 390 J/g, better dispersions are obtained. The stability of the dispersion over time was evaluated over 13 weeks using UV-vis spectroscopy and Zeta Potential. With the most relevant data collected, sonication energies of 190, 390 and 490 J/g, at 10 mM were selected at the first and the fourth week of storage to obtain Portland cement specimens. Finally, we found an improvement of the mechanical properties of the samples built with Portland cement and solutions stored for one and four weeks; it can be concluded that the MWCNTs improved the hydration period.