AIM: To develop and evaluate the efficacy of synthesised strontium-doped nano hydroxyapatite dentifrice and compare its remineralizing potential with a topical cream containing Casein Phospho Peptide - Amorphous Calcium Phosphate, in remineralizing artificial carious lesion on enamel. MATERIALS AND METHODS: Enamel specimens of 4 x 4 x 1 mm were prepared from 90 freshly extracted teeth. Specimens were divided into 3 groups of 30 samples each, based on the type of dentifrice applied that is a control group (Group I) and two experimental groups (Groups II, III). Surface topography and the calcium/phosphorous ratio of all sound specimen were evaluated using Scanning electron microscope and Energy Dispersive X-ray Analysis (SEM-EDAX). The samples in group I and each of the experimental groups were subjected to demineralisation and the calcium/phosphorous ratio of the demineralized specimen were analysed. The samples were then subjected to remineralisation using different agents in each group. Samples in the control group (Group I) were brushed with a conventional dentifrice. In the experimental groups, Group II topical cream with Casein Phosphopeptide and Amorphous Calcium phosphate (CPP-ACP) was used and in Group III laboratory synthesized Strontium-doped nanohydroxyapatite paste (Sr-nHAP), respectively for 28 consecutive days. The samples in the both the control and the two experimental groups were again subjected to SEM-EDAX analysis to analyse the calcium phosphorus ratio following remineralisation cycle. Groupwise comparison of the data was done with one way ANOVA followed by Tukeys Post hoc Test. RESULTS: Both experimental groups (II, III) showed statistically significant remineralisation potential after demineralisation, compared to the control group I. Intergroup comparison showed that the samples in Group III showed the higher remineralisation potential than Group II and was statistically significant. CONCLUSION: Both CPP- ACP containing tooth cream as well as Sr doped nHAp showed remineralisation potential. Sr doped nanohydroxyapatite showed better remineralisation than CPP ACP and can be considered for enamel repair in incipient carious lesions.