Mechanical Properties of PALF/Kevlar-Reinforced Unsaturated Polyester Hybrid Composite Laminates.

Natural and synthetic fibres are in high demand due to their superior properties. Natural fibres are less expensive and lighter as compared to synthetic fibres. Synthetic fibres have drawn much attention, especially for their outstanding properties, such as durability, and stability. The hybridisation between natural and synthetic fibres composite are considered as an alternative to improve the current properties of natural and synthetic fibres. Therefore, this study aimed to determine the physical and mechanical properties of pineapple leaf fibre (PALF) and Kevlar reinforced unsaturated polyester (UP) hybrid composites. The PALF/Kevlar hybrid composites were fabricated by using hand layup method utilising unsaturated polyester as the matrix. These composites were laid up to various laminated configurations, such as [PKP]s, [PPK]s, [KPP]s, [KKP]s, [PPP]s and [KKK]s, whereby PALF denoted as P and Kevlar denoted as K. Next, they were cut into size and dimensions according to standards. Initially, the density of PALF/Kevlar reinforced unsaturated polyester were evaluated. The highest density result was obtained from [KKK]s, however, the density of hybrid composites was closely indistinguishable. Next, moisture absorption behaviour and its effects on the PALF/Kevlar reinforced unsaturated polyester were investigated. The water absorption studies showed that the hybridisation between all PALF and Kevlar specimens absorbed moisture drastically at the beginning of the moisture absorption test and the percentage of moisture uptake increased with the volume fraction of PALF in the samples. The tensile test indicated that all specimens exhibited nonlinear stress-strain behaviour and shown a pseudo-ductility behaviour. [KKP]s and [KPK]s hybrid composites showed the highest tensile strength and modulus. The flexural test showed that [KPK]s had the highest flexural strength of 164.0 MPa and [KKP]s had the highest flexural modulus of 12.6 GPa. In terms of the impact strength and resistance, [KKP]s outperformed the composite laminates. According to SEM scans, the hybrid composites demonstrated a stronger interfacial adhesion between the fibres and matrix than pure PALF composite.

Physical, Mechanical and Perforation Resistance of Natural-Synthetic Fiber Interply Laminate Hybrid Composites.

Natural and synthetic fibres have emerged in high demand due to their excellent properties. Natural fibres have good mechanical properties and are less expensive, making them a viable substitute for synthetic fibers. Owing to certain drawbacks such as their inconsistent quality and hydrophilic nature, researchers focused on incorporating these two fibres as an alternative to improve the limitations of the single fibre. This review focused on the interply hybridisation of natural and synthetic fibres into composites. Natural fibres and their classifications are discussed. The physical and mechanical properties of these hybrid composites have also been included. A full discussion of the mechanical properties of natural/synthetic fibre hybrid composites such as tensile, flexural, impact, and perforation resistance, as well as their failure modes, is highlighted. Furthermore, the applications and future directions of hybrid composites have been described in details.

Dynamic Mechanical Properties and Thermal Properties of Longitudinal Basalt/Woven Glass Fiber Reinforced Unsaturated Polyester Hybrid Composites.

This study investigates the mechanical, thermal, and chemical properties of basalt/woven glass fiber reinforced polymer (BGRP) hybrid polyester composites. The Fourier transform infrared spectroscopy (FTIR) was used to explore the chemical aspect, whereas the dynamic mechanical analysis (DMA) and thermomechanical analysis (TMA) were performed to determine the mechanical and thermal properties. The dynamic mechanical properties were evaluated in terms of the storage modulus, loss modulus, and damping factor. The FTIR results showed that incorporating single and hybrid fibers in the matrix did not change the chemical properties. The DMA findings revealed that the B7.5/G22.5 composite with 7.5 wt% of basalt fiber (B) and 22.5 wt% of glass fiber (G) exhibited the highest elastic and viscous properties, as it exhibited the higher storage modulus (8.04 × 109 MPa) and loss modulus (1.32 × 109 MPa) compared to the other samples. All the reinforced composites had better damping behavior than the neat matrix, but no further enhancement was obtained upon hybridization. The analysis also revealed that the B22.5/G7.5 composite with 22.5 wt% of basalt fiber and 7.5 wt% of glass fiber had the highest Tg at 70.80 °C, and increased by 15 °C compared to the neat matrix. TMA data suggested that the reinforced composites had relatively low dimensional stabilities than the neat matrix, particularly between 50 to 80 °C. Overall, the hybridization of basalt and glass fibers in unsaturated polyester formed composites with higher mechanical and thermal properties than single reinforced composites.