In this work, the effect of the addition of noble metals on the order-order disorder process of the L12 structure corresponding to the intermetallic Ni3Al is analyzed. Stoichiometric, nonstoichiometric, and quasi-binary compositions doped with noble metals such as Ag, Au, Pd, and Pt (1 at%) were analyzed. It was observed that depending on the composition, there is a modification in the activation energies calculated from the two time constants that characterize the disorder process. The statistic of atomic jumps was typified based on the configuration of the window to be crossed and, with this, it was identified that the origin of the negative activation energy of the long disorder process is due to an increase in the corresponding energy of the AlAl-Ni jump through unnatural windows.
RESUMO
In this study, the performance evaluation of lanthanum compounds as corrosion inhibitors of vanadium salts was performed. The inhibitors tested were lanthanum acetate and La2O3. The performance of the inhibitors was tested using sodium metavanadate (NaVO3) as a corrosive medium at 700, 800, and 900 °C. The corrosion inhibitory effect was evaluated on the corrosion process of 304H stainless steel. The corrosion rate of the steel was determined by the mass loss technique after 100 h of immersion in the corrosive salt with and without the addition of the corrosion inhibitor. The results show that lanthanum compounds act as corrosion inhibitors of vanadium salts. The inhibitory effect increases by increasing the concentration and tends to decrease when increasing the test temperature. Lanthanum compounds act as excellent corrosion inhibitors due to their ability to stabilize vanadium cations. Vanadium is stabilized by forming a new compound, lanthanum vanadate (LaVO4), with a melting point much higher than the compounds formed when Mg or Ni compounds are used as corrosion inhibitors.