RESUMO
Electrode materials must be rationally designed with morphologies and electroactive sites manipulated through cations' synergy in bimetal compounds in order to maximize the performance of energy storage devices. Therefore, the present study emphasizes binder-free scalable preparation of cobalt nickel vanadate (CNV) thin films by a facile successive ionic layer adsorption and reaction (SILAR) approach with specific cations (Co:Ni) alternation. Increasing the Ni cation content in the CNV notably transforms its microflower structure comprising nanoflakes (252 nm) into nanoparticles (74 nm). An optimized S-CNV5 thin film cathode with Co:Ni molar ratio of â¼ 0.4:0.6 and a high specific surface area of 340 m2 g-1, provided the excellent specific capacitance (Csp) and capacity (Csc) of 1382 F g-1 and 691 C g-1, respectively at 1 A g-1 current density. A hybrid aqueous supercapacitor (HASc) device with positive and negative electrodes comprising optimized CNV and reduced graphene oxide (rGO), respectively, in a 1 M KOH electrolyte delivered a Csp of 133 F g-1 and a specific energy (SE) of 53 Wh kg-1 at a specific power (SP) of 2261 kW kg-1. Additionally, a fabricated hybrid solid-state supercapacitor (HSSc) device with the same electrodes applying PVA-KOH gel electrolyte displayed a Csp of 119 F g-1, and SE of 46 Wh kg-1 at SP of 1184 W kg-1. This boosted electrochemical activity is due to the synergetic effects of Ni and Co species in the CNV thin film electrodes, emphasizing the potential of CNV electrodes as cathodes in hybrid energy storage devices.
RESUMO
Silica aerogels and their derivatives have outstanding thermal properties with exceptional values in the thermal insulation industry. However, their brittle nature restricts their large-scale commercialization. Thus, enhancing their mechanical strength without affecting their thermal insulating properties is essential. Therefore, for the first time, highly thermally stable poly(acrylamide-co-acrylic acid) partial sodium salt is used as a reinforcing polymer to synthesize hybrid P(AAm-CO-AAc)-silica aerogels via epoxy ring-opening polymerization in the present study. Functional groups in P(AAm-CO-AAc) partial sodium salts, such as CONH2 and COOH, acted as nucleophiles for the epoxy ring-opening reaction with (3-glycidyloxypropyl)trimethoxysilane, which resulted in a seven-fold enhancement in mechanical strength compared to that of pristine silica aerogel while maintaining thermal conductivity at less than 30.6 mW/mK and porosity of more than 93.68%. Moreover, the hybrid P(AAm-CO-AAc)-silica aerogel demonstrated improved thermal stability up to 343 °C, owing to the synergetic effect between the P(AAm-CO-AAc) and the silica aerogel, corresponding to the thermal stability and strong covalent bonding among them. These excellent results illustrate that this new synthetic approach for producing hybrid P(AAm-CO-AAc)-silica aerogels is useful for enhancing the mechanical strength of pristine silica aerogel without impairing its thermal insulating property and shows potential as an industrial heat insulation material.