Laser-Induced Interdigital Structured Graphene Electrodes Based Flexible Micro-Supercapacitor for Efficient Peak Energy Storage.

The rapidly developing demand for lightweight portable electronics has accelerated advanced research on self-powered microsystems (SPMs) for peak power energy storage (ESs). In recent years, there has been, in this regard, a huge research interest in micro-supercapacitors for microelectronics application over micro-batteries due to their advantages of fast charge-discharge rate, high power density and long cycle-life. In this work, the optimization and fabrication of micro-supercapacitors (MSCs) by means of laser-induced interdigital structured graphene electrodes (LIG) has been reported. The flexible and scalable MSCs are fabricated by CO2-laser structuring of polyimide-based Kapton ® HN foils at ambient temperature yielding interdigital LIG-electrodes and using polymer gel electrolyte (PGE) produced by polypropylene carbonate (PPC) embedded ionic liquid of 1-ethyl-3-methyl-imidazolium-trifluoromethansulphonate [EMIM][OTf]. This MSC exhibits a wide stable potential window up to 2.0 V, offering an areal capacitance of 1.75 mF/cm2 at a scan rate of 5.0 mV/s resulting in an energy density (Ea) of 0.256 µWh/cm2 @ 0.03 mA/cm2 and power density (Pa) of 0.11 mW/cm2 @0.1 mA/cm2. Overall electrochemical performance of this LIG/PGE-MSC is rounded with a good cyclic stability up to 10,000 cycles demonstrating its potential in terms of peak energy storage ability compared to the current thin film micro-supercapacitors.

Application of Ionic Liquids for Batteries and Supercapacitors.

Nowadays, the rapid development and demand of high-performance, lightweight, low cost, portable/wearable electronic devices in electrical vehicles, aerospace, medical systems, etc., strongly motivates researchers towards advanced electrochemical energy storage (EES) devices and technologies. The electrolyte is also one of the most significant components of EES devices, such as batteries and supercapacitors. In addition to rapid ion transport and the stable electrochemical performance of electrolytes, great efforts are required to overcome safety issues due to flammability, leakage and thermal instability. A lot of research has already been completed on solid polymer electrolytes, but they are still lagging for practical application. Over the past few decades, ionic liquids (ILs) as electrolytes have been of considerable interest in Li-ion batteries and supercapacitor applications and could be an important way to make breakthroughs for the next-generation EES systems. The high ionic conductivity, low melting point (lower than 100 °C), wide electrochemical potential window (up to 5-6 V vs. Li+/Li), good thermal stability, non-flammability, low volatility due to cation-anion combinations and the promising self-healing ability of ILs make them superior as "green" solvents for industrial EES applications. In this short review, we try to provide an overview of the recent research on ILs electrolytes, their advantages and challenges for next-generation Li-ion battery and supercapacitor applications.

Efficient Flexible All-Solid Supercapacitors with Direct Sputter-Grown Needle-Like Mn/MnOx@Graphite-Foil Electrodes and PPC-Embedded Ionic Electrolytes.

Recent critical issues regarding next-generation energy storage systems concern the cost-effective production of lightweight, safe and flexible supercapacitors yielding high performances, such as high energy and power densities as well as a long cycle life. Thus, current research efforts are concentrated on the development of high-performance advance electrode materials with high capacitance and excellent stability and solid electrolytes that confer flexibility and safety features. In this work, emphasis is placed on the binder-free, needle-like nanostructured Mn/MnOx layers grown onto graphite-foil deposited by reactive sputtering technique and to the polymer gel embedded ionic electrolytes, which are to be employed as new flexible pseudocapacitive supercapacitor components. Microstructural, morphological and compositional analysis of the layers has been investigated by X-ray diffractometer (XRD), Field Emission Scanning Electron Microscope (FE-SEM) and X-ray photoelectron spectroscopy (XPS). A flexible lightweight symmetric pouch-cell solid-state supercapacitor device is fabricated by sandwiching a PPC-embedded ionic liquid ethyl-methylimidazolium bis (trifluoromethylsulfonyl) imide (EMIM)(TFSI) polymer gel electrolyte (PGE) between two Mn/MnOx@Graphite-foil electrodes and tested to exhibit promising supercapacitive behaviour with a wide stable electrochemical potential window (up to 2.2 V) and long-cycle stability. This pouch-cell supercapacitor device offers a maximum areal capacitance of 11.71 mF/cm2@ 0.03 mA/cm2 with maximum areal energy density (Ea) of 7.87 mWh/cm2 and areal power density (Pa) of 1099.64 mW/cm2, as well as low resistance, flexibility and good cycling stability. This supercapacitor device is also environmentally safe and could be operated under a relatively wide potential window without significant degradation of capacitance performance compared to other reported values. Overall, these rationally designed flexible symmetric all-solid-state supercapacitors signify a new promising and emerging candidate for component integrated storage of renewable energy harvested current.

Studies on Magnetic and Dielectric Properties of Antiferromagnetically Coupled Dinuclear Cu(II) in a One-Dimensional Cu(II) Coordination Polymer.

A one-dimensional Cu(II) coordination polymer with encapsulated antiferromagnetically coupled binuclear Cu(II) has been synthesized by using 5-nitroisophthalic acid (5-N-IPA) and 4-aminopyridine (4-APY) [Cu2(5-N-IPA)2(4-APY)4] n (1). Electrical properties are examined by complex impedance (Z*), dielectric permittivity (ε*), and ac conductivity studies at different frequencies (10 kHz-5 MHz) and temperatures (253-333 K). The contribution of grain and grain boundary has been explained by a different theoretical model. The variable temperature magnetic susceptibility data for compound 1 were recorded between 300 and 2 K. The shape of the curve (χM T vs T) indicates dominant antiferromagnetic coupling, which results from the interaction between the copper(II) atoms.

Electrochemical Energy Storage Properties of Ni-Mn-Oxide Electrodes for Advance Asymmetric Supercapacitor Application.

In this work, we report a facile one-spot synthesis process and the influence of compositional variation on the electrochemical performance of Ni-Mn-oxides (Ni:Mn = 1:1, 1:2, 1:3, and 1:4) for high-performance advanced energy storage applications. The crystalline structure and the morphology of these synthesized nanocomposites have been demonstrated using X-ray diffraction, field emission scanning electron microscopy, and transmission electron Microscopy. Among these materials, Ni-Mn-oxide with Ni:Mn = 1:3 possesses a large Brunauer?Emmett?Teller specific surface area (127 m2 g?1) with pore size 8.2 nm and exhibits the highest specific capacitance of 1215.5 F g?1 at a scan rate 2 mV s?1 with an excellent long-term cycling stability (?87.2% capacitance retention at 10 A g?1 over 5000 cycles). This work also gives a comparison and explains the influence of different compositional ratios on the electrochemical properties of Ni-Mn-oxides. To demonstrate the possibility of commercial application, an asymmetric supercapacitor device has been constructed by using Ni-Mn-oxide (Ni:Mn = 1:3) as a positive electrode and activated carbon (AC) as a negative electrode. This battery-like device achieves a maximum energy density of 132.3 W h kg?1 at a power density of 1651 W kg?1 and excellent coulombic efficiency of 97% over 3000 cycles at 10 A g?1.