RESUMO
Traumatized anterior teeth require quick functional and esthetic repair. Tooth fragment reattachment is a simple and conservative clinical procedure to restore fractured anterior teeth. Different techniques of reattachment include enamel beveling, "v-" shaped internal enamel and dentin grooves, external chamfer, over contouring, and by placing fiber post, all of which were invasive methods. This article describes a novel technique of reattachment using canal projectors for stabilizing fractured fragments followed by endodontic therapy and internal reinforcement with custom fiber post (everStick Post™, GC Corporation, Tokyo, Japan).
RESUMO
AIM: The aim and purpose of this study was to determine the occlusal fracture resistance of three core buildup materials using the Nayyar technique. MATERIALS AND METHODS: Thirty human extracted maxillary premolars were used for the study. The test samples were decoronated till the cementoenamel junction (CEJ) and proper cleaning and shaping was done with protaper niti files till the F3. Corresponding f3 protaper(Dentysply)gutta pecha cones were selected and obturated. The gutta-percha was removed till the depth of 4 mm from the coronal orifice with Gates Glidden (GG) drills for all the samples; then the samples were randomly divided into three different groups. Group I was restored with universal composite Z350XT, group II was restored with light curable glass ionomer cement (GIC), and group III was restored with miracle mix. The coronal buildup was done using compound supported matrix. The fracture resistance strength of all the specimen groups was tested under a universal testing machine. RESULTS: The data of the study were statistically analyzed by one-way analysis of variance (ANOVA) and Bonferroni's comparison test. Results of the study showed that group I that was restored with the universal composite Z350XT showed much higher fracture resistance strength compared to the other two groups. Statistically significant difference was noted between group I and group II and also between group I and group III. CONCLUSION: It can be concluded that the core buildup done with composite offered better occlusal fracture resistance strength compared to light curable GIC and miracle mix.
RESUMO
AIM: To determine the shear bond strength of self-etch adhesive G-bond on pre-etched enamel. MATERIALS AND METHODS: Thirty caries free human mandibular premolars extracted for orthodontic purpose were used for the study. Occlusal surfaces of all the teeth were flattened with diamond bur and a silicon carbide paper was used for surface smoothening. The thirty samples were randomly grouped into three groups. Three different etch systems were used for the composite build up: group 1 (G-bond self-etch adhesive system), group 2 (G-bond) and group 3 (Adper single bond). Light cured was applied for 10 seconds with a LED unit for composite buildup on the occlusal surface of each tooth with 8 millimeters (mm) in diameter and 3 mm in thickness. The specimens in each group were tested in shear mode using a knife-edge testing apparatus in a universal testing machine across head speed of 1 mm/ minute. Shear bond strength values in Mpa were calculated from the peak load at failure divided by the specimen surface area. The mean shear bond strength of all the groups were calculated and statistical analysis was carried out using one-way Analysis of Variance (ANOVA). RESULTS: The mean bond strength of group 1 is 15.5 Mpa, group 2 is 19.5 Mpa and group 3 is 20.1 Mpa. Statistical analysis was carried out between the groups using one-way ANOVA. Group 1 showed statistically significant lower bond strength when compared to groups 2 and 3. No statistical significant difference between groups 2 and 3 (p < 0.05). CONCLUSION: Self-etch adhesive G-bond showed increase in shear bond strength on pre-etched enamel.