RESUMO
Alkali metal doping is essential to achieve highly efficient energy conversion in Cu(In,Ga)Se2 (CIGSe) solar cells. Doping is normally achieved through solid state reactions, but recent observations of gas-phase alkali transport in the kesterite sulfide (Cu2ZnSnS4) system (re)open the way to a novel gas-phase doping strategy. However, the current understanding of gas-phase alkali transport is very limited. This work (i) shows that CIGSe device efficiency can be improved from 2% to 8% by gas-phase sodium incorporation alone, (ii) identifies the most likely routes for gas-phase alkali transport based on mass spectrometric studies, (iii) provides thermochemical computations to rationalize the observations and (iv) critically discusses the subject literature with the aim to better understand the chemical basis of the phenomenon. These results suggest that accidental alkali metal doping occurs all the time, that a controlled vapor pressure of alkali metal could be applied during growth to dope the semiconductor, and that it may have to be accounted for during the currently used solid state doping routes. It is concluded that alkali gas-phase transport occurs through a plurality of routes and cannot be attributed to one single source.
RESUMO
Controlling the Ga incorporation of Cu-In-Ga metal precursors for Cu(In,Ga)Se2 (CIGS) solar cells is one of the main challenges for low cost electrodeposition processes, mainly due to the difficulty in electrodepositing metallic Ga from aqueous electrolytes. In this work we use the deep eutectic solvent (DES) Choline Chloride : Urea (ChCl : U - 1 : 2) to efficiently codeposit In-Ga on Cu and Mo electrodes. We control the Ga/(Ga+In) (Ga/III) ratio of the films via the mass fluxes. The electrochemical behavior of ChCl : U containing GaCl3 and InCl3 is studied by rotating disk electrode cyclic voltammetry (CV) on Mo and Cu electrodes. CV revealed on both Mo and Cu electrodes that the electrochemical behavior of the ChCl : U-GaCl3-InCl3 system is the superposition of the individual In and Ga electrochemistry. On a Cu electrode the morphology, crystal structure and element distribution of the deposits were a function of the Ga/III ratio. We demonstrate the precise control of Ga incorporation over a large composition range from 0.1 ≤ Ga/III ≤ 0.9 and proved that ED from DES is a straightforward, robust and efficient process. First solar cells based on Mo/Cu/In-Ga metal stacks achieved efficiencies as high as 7.9% with a Voc of 520 mV.