Melamine Network as a Solution for Significant Enhancement of the Mechanical, Adsorptive, and Surface Properties in a Novel Carbon Nanomaterial-Silica Aerogel Composite.

Silica aerogels exhibit exceptional characteristics such as mesoporosity, light weight, high surface area, and pore volume. Nevertheless, their utilization in industrial settings remains constrained due to their brittleness, moisture sensitivity, and costly synthesis procedure. Several studies have proved that adding nanofillers, such as carbon nanotubes (CNT) or graphene nanoplatelets (GNP), can improve the mechanical strength of the aerogels. The incorporation of nanofillers is often accompanied by agglomeration and pore blockage, which, in turn, deteriorates the surface area, pore volume, and low density. Including flexible melamine foam (MF) as a scaffold for the silica aerogel and nanofiller composite can prevent the restacking of the nanofillers through π-π interaction, hence maintaining the incredible properties of aerogels and improving their mechanical properties. CNT, GNP, and the polymeric silica precursor, polyvinyltrimethoxysilane (PVTMS), were added to a MF, at varying concentrations, to fabricate the MF-aerogel nanocomposites. Surfactant and sonication were utilized to ensure a homogeneous dispersion of the nanofillers in the system. The presence of MF prevented the agglomeration of nanofillers, resulting in lower density and relatively higher surface properties (SBET up to 929 m2·g-1 and pore volume up to 4.34 cc·g-1). Moreover, the MF-supported samples could endure 80% strain without breakage and showed an outstanding compressive strength of up to ∼20 MPa. These aerogel nanocomposites also demonstrated an excellent volatile organic compound (∼2680 mg·g-1) and cationic dye adsorption (∼10 mg·g-1).

Efficient Electromagnetic Wave Absorption and Thermal Infrared Stealth in PVTMS@MWCNT Nano-Aerogel via Abundant Nano-Sized Cavities and Attenuation Interfaces.

Pre-polymerized vinyl trimethoxy silane (PVTMS)@MWCNT nano-aerogel system was constructed via radical polymerization, sol-gel transition and supercritical CO2 drying. The fabricated organic-inorganic hybrid PVTMS@MWCNT aerogel structure shows nano-pore size (30-40 nm), high specific surface area (559 m2 g-1), high void fraction (91.7%) and enhanced mechanical property: (1) the nano-pore size is beneficial for efficiently blocking thermal conduction and thermal convection via Knudsen effect (beneficial for infrared (IR) stealth); (2) the heterogeneous interface was beneficial for IR reflection (beneficial for IR stealth) and MWCNT polarization loss (beneficial for electromagnetic wave (EMW) attenuation); (3) the high void fraction was beneficial for enhancing thermal insulation (beneficial for IR stealth) and EMW impedance match (beneficial for EMW attenuation). Guided by the above theoretical design strategy, PVTMS@MWCNT nano-aerogel shows superior EMW absorption property (cover all Ku-band) and thermal IR stealth property (ΔT reached 60.7 °C). Followed by a facial combination of the above nano-aerogel with graphene film of high electrical conductivity, an extremely high electromagnetic interference shielding material (66.5 dB, 2.06 mm thickness) with superior absorption performance of an average absorption-to-reflection (A/R) coefficient ratio of 25.4 and a low reflection bandwidth of 4.1 GHz (A/R ratio more than 10) was experimentally obtained in this work.